Graphite Electrode

Description:
Graphite electrode: Graphite electrode is mainly usde for steel-making in electric furnace, mineral hot furnace and electric resistance furnace. Graphite electrode conducts electric current into the furnace. Electric current produces arc in the smelting district in the electric furnace, when the temperature increase to about 2000c, smelting begins. Our a series of graphite electrode is applicable to the common furnace and high power furnace with high pressure and short arc.
Specifications and properties:
Np graphite electrode:
1. dia100-350mm, resistivity 6-9, bending strength 10-12mpa, elastic modulus 7-9gpa, cte1.8-2.9 x 10-6/c, compressive strength18-22 mpa, bulk density 1.52-1.57g/cm3, ash 0.3%.
2. dia 400-500mm, resistivity 7-10, bending strength 6.5-10mpa, elastic modulus 7-9.3gpa, cte 1.7-2.9 x 10-6/c, compressive strength 18-22 mpa, bulk density 1.52-1.57g/cm3, ash0.3%.
HP graphite electrode:
1. dia200-350mm, resistivity 6-7, bending strength 10-15mpa, elastic modulus 9-12gpa, cte 1.6-2.2 x 10-6/c, compressive strength 24-28 mpa, bulk density 1.62-1.70g/cm3, ash 0.3%.
2. dia 400-500mm, resistivity 6-7, bending strength 10-13mpa, elastic modulus 9-12gpa, cte 1.5-2.2 x 10-6/c, compressive strength 24-26 mpa, bulk density 1.62-1.68g/cm3, ash 0.3%.
Graphite electrode nipple: Dia 200-500mm, resistivity 4-7, bending strength 12-20mpa, elastic mosulus12-14gpa, cte2.0-3.0 x 10-6/c, compressive strength 32-38 mpa, bulk density 1.70-1.80g/cm3, ash 0.3%.