100% Virgin Polyethylene Granule / Virgin HDPE for Extrusion Blow-Bottles
| Price | $1020.00 |
|---|---|
| Min Order | 20 Tons |
| Availability | In Stock |
| Shipping From | Beijing, China |
| Popularity | 329 people viewed |
Model NO.:
HDPE 5502; 5000S, 7000f
CAS No.:
9002-88-4
Formula:
-[-CH2-CH2-]N
EINECS:
9002-88-4
Material:
High Density Polyethylene/HDPE
Usage:
General Plastics
Plastic Properties After Heated:
Thermoplastic Plastics
Plastic Forming Method:
Film/Blow/Injection/Extrusion
Color:
According to Your Demand
Type:
HDPE
Payment:
T/T L/C
Delivery:
Wihin 10 Days After Receiving Deposit
Transport Package:
25kg/Bag
Specification:
international standard
Origin:
China
HS Code:
3901902000
Product Description
1.Pictures
2. virgin hdpe granules Characteristic
This HDPE granulate is the extrusion, pipe grade with good weather resistance,good dispersion of black carbon also excellent resistance to rapid crack propagation resistance and slow crack growth performance.
3.Virgin & Recycled PE granules
1>. Blow molding grade,
2>. Injection molding grade,
3>. Film grade;
4>. Extrusion grade.
4.Specification
2. virgin hdpe granules Characteristic
This HDPE granulate is the extrusion, pipe grade with good weather resistance,good dispersion of black carbon also excellent resistance to rapid crack propagation resistance and slow crack growth performance.
3.Virgin & Recycled PE granules
1>. Blow molding grade,
2>. Injection molding grade,
3>. Film grade;
4>. Extrusion grade.
4.Specification
HDPE cable material Property | Unit | Typical Value |
Mass density | g/cm³ | 0.941-0.959 |
Melt flow Rate(190 Centigrade /2.16kg) | g/10min | ≤1.0 |
Tensile yield strength | MPa | ≥19.0 |
Flexural modulus | Mpa | ≥965 |
Elongation@ break | % | ≥400 |
Impact Embrittlement temperature | Centigrade | MAX -118 |
Dielectric Constant | 100KHZ | 2.32 |
1MHZ | 2.31 | |
Loss Tangent | 100KHZ | MAX 0.0001 |
1MHZ | MAX 0.0001 | |
Volume resistivity | OHM-CM | MIN 1x10 15 |
| Item | Test method | Test data | Data unit |
| MFR(190ºC,2.16KG) | ASTM D1238 | 0.3 | g/10min |
| Density | ASTM D792 | 0.956 | g/cm³ |
| Tensile yield strength | ASTM D638 | 25 | Mpa |
| Tensile breaking strength | ASTM D638 | 38 | Mpa |
| flexural modulus (2% secant) | ASTM D790 | 860 | Mpa |
| Elongation at break | ASTM D638 | 950 | % |
| Environmental stress cracking resistance (50°C, 100% Igepal, F50) | ASTM D1693 | >200 | hr |
| Vicat softening point | ASTM D1525 | 128 | ºC |
| Notched impact strength of cantilevered beams(23ºC) | ASTM D256 | 130 | J/m |
| Shore hardness(D) | ASTM D2240 | 66 |