1K Pan Fiber Precursor
| Price | $95.00 |
|---|---|
| Min Order | 36 kg |
| Availability | In Stock |
| Shipping From | Guangdong, China |
| Popularity | 227 people viewed |
Model NO.:
XG-1K
Model:
Xg-1K
Filament Number:
1K
Linear Density:
120tex
Linear Density of Monofilament:
0.122+/-0.003tex
Linear Density Deviation From Nominal:
Max.+/-5%
Tensile Strenght for Single Fiber:
Min.58 Cn/Tex
Elongation at Break:
12+/-3%
Oil Content:
1.2+/-0.5%
Humidity:
<0.1%
Material:
100% Acrylic
Feature:
Anti-Pilling, Abrasion-Resistant, Anti-Distortion
Fiber Type:
Filament
Color:
White
Function:
High Strength Fiber
Structure:
Synthetic Carbon Chain
Usage:
Carbon Fiber Production
Pattern:
No
Width:
1mm
Trademark:
XIANGU
Transport Package:
Cartons
Specification:
ROHS
Origin:
Guangdong
HS Code:
5503300000
Product Description
1k PAN Fiber Precursor
Acrylic fiber for carbon fiber is high purity and high strength fiber through wet-two step method with solvent DMF and surface finishing size treatment.It has higher elastic modulus,tensile strength and anti-UV properties,anti-high temperature and cold performance.It is the best raw material of PAN carbon fiber Via Pre-oxidation(200~300ºC),carbonization(1000~1500ºC), Graphitization(2500~3000ºC).
SPECIFICATIONS:
APPLICATION FIELDS:
carbon fiber roving productions or carbon fiber filament manufacturing.
STORAGE:
The polyacrylonitrile precursor should be keep dry in their original cartons and stored in a suitable place,preferably at room temperature with 35-65% relative humidity.Avoid the sun, rain and fire
PACKAGING:
PRODUCT DETAIL IMAGES:
Acrylic fiber for carbon fiber is high purity and high strength fiber through wet-two step method with solvent DMF and surface finishing size treatment.It has higher elastic modulus,tensile strength and anti-UV properties,anti-high temperature and cold performance.It is the best raw material of PAN carbon fiber Via Pre-oxidation(200~300ºC),carbonization(1000~1500ºC), Graphitization(2500~3000ºC).
SPECIFICATIONS:
| MODEL | XG-1K |
| FILAMENT NUMBER | 1K |
| LINEAR DENSITY | 120tex |
| LINEAR DENSITY OF MONOFILAMENT | 0.122 ±0.003tex |
| LINEAR DENSITY DEVIATION FROM NOMINAL | Max.±5% |
| TENSILE STRENGHT FOR SINGLE FIBER | Min.58 cN/tex |
| ELONGATION AT BREAK | 12±3% |
| OIL CONTENT | 1.2±0.5% |
| HUMIDITY | ≤0.1% |
APPLICATION FIELDS:
carbon fiber roving productions or carbon fiber filament manufacturing.
STORAGE:
The polyacrylonitrile precursor should be keep dry in their original cartons and stored in a suitable place,preferably at room temperature with 35-65% relative humidity.Avoid the sun, rain and fire