42CrMo4 DIN 1.7225 4140 Super-Strength Tool Steel Bar Scm440

Price $5000.00
Min Order 1 Ton
Availability In Stock
Shipping From Jiangsu, China
Popularity 422 people viewed
Send Inquiry View Full Page
Model NO.:
4140
Standard:
DIN, JIS, AISI, ASTM, GB, BS
Technics:
Hot Rolled
Application:
Tool Steel Bar
Surface:
Polished
Alloy:
Alloy
Special Use:
High-strength Steel Plate
Ts (MPa):
>1080
Elongation Stress (MPa):
930
Elongation:
45
Eduction of Area:
63
Melting Point:
1150
Certificate:
SGS ISO
Delivery Time:
Within 15working Days
Trademark:
Taixie
Transport Package:
Woven Bag, Wooden Box
Specification:
from 5mm--100mm
Origin:
Wuxi, Jiangsu
HS Code:
72222000
Product Description


Chemical Component%
CSiCrMnCuSPNiMo
0.38~0.450.17~0.370.90~1.20.5~0.8≤0.3≤0.035≤0.035≤0.30.15~0.25
EN 1.7225---4140 is a high alloy austenitic stainless steel. The grade is intended for use under severe corrosive conditions. The steel grade was originally developed to resist corrosion in dilute sulphuric acid. EN 1.7225 is fully austenitic, and is less sensitive to precipitation of ferrite and sigma phase than conventional austenitic grades with high molybdenum content. Due to the combination of relatively high contents of chromium, nickel, molybdenum and copper,   EN 1.7225 has good resistance to general corrosion, particulary in dilute sulphuric acid.  It is non-magnetic in the annealed condition but may become slightly magnetic as a result of cold-working or welding.
Design features  
⇒ Good resistance to uniform corrosion
⇒ Good resistance to pitting and crevice corrosion  
⇒ Very good resistance to stress corrosion cracking
⇒ Good resistance to intercrystalline corrosion
⇒ Good formability and weldability
Corrosion resistance  
Uniform corrosion Uniform corrosion is characterized by a uniform corrosion of the steel surface in contact with the corrosive medium. Resistance is normally considered good if the corrosion rate is less than 0.1 mm/year. As a result of its high chromium, nickel and molybdenum contents and its alloying with copper, EN 1.7225 is passivated even in reducing environments such as dilute sulphuric acid and formic acid. Its high nickel content contributes towards its relatively low corrosion rate in the active state.  
Intercrystalline corrosion  
EN 1.7225 has a very low carbon content. This means that there is very little risk of carbide precipitation in connection with ordinary heat treatment and welding. The risk of intercrystalline corrosion after ordinary heat treatment and welding is thereby eliminated.