Aluminium Casting and Machining Side Main Bracket
| Price | $127.40 |
|---|---|
| Min Order | 50 Pieces |
| Availability | In Stock |
| Shipping From | Zhejiang, China |
| Popularity | 519 people viewed |
Model NO.:
S-2002
Type:
Clay Wet Sand
Casting Method:
Thermal Gravity Casting
Sand Core Type:
Resin Sand Core
Application:
Machinery Parts
Machining:
CNC Machining
Material:
Aluminium & Aluminum Alloy
Surface Treatment:
Electroplating
Surface Roughness:
Ra3.2
Standard:
DIN
Certification:
CE, ISO 9001:2008
Quality Grade:
AAA
Inspection Class:
A1
Difficulty Class:
A2
Mould Type:
Metal
Trademark:
YY
Transport Package:
Carton and Wooden Box
Specification:
550x360x330, 9.1kg
Origin:
China
HS Code:
8462319000
Product Description
This part made by sand casting with 1 resin cores.
After CNC machining, The part need to be elctroplating carefully .
Material is Al alloy Al Si7Mg ,T5 treatment.
A layer of screened fine surface sand is firstly covered on the aluminum mold, then pour in the back sand and hammer it tightly, use flame to dry the surface moisture, carefully place the resin sand core.
With effective degassing to reduce hydrogen, the aluminum liquid is poured into the mold cavity . After cooling, take out the parts, and a beautiful aluminum alloy artwork is displayed in front of us.
By the numerical control hot-box core shooter machine, we can manufacture precision dimensions and high-strength cores, strictly controlling the raw resin sand and the temperature & time parameters of heating. Therefore, the excellent cavity ensures the beautiful surface and good dimensional tolerance of these aluminum products.
After CNC machining, the perfect finished product is successfully made. Especially suitable for manifold and pump or valve components with complex cavities and high pressure requirement.
Our manual molding process is suitable for complex aluminum and copper castings,the mold and casting costs are relatively low and be competitive.
After CNC machining, The part need to be elctroplating carefully .
Material is Al alloy Al Si7Mg ,T5 treatment.
A layer of screened fine surface sand is firstly covered on the aluminum mold, then pour in the back sand and hammer it tightly, use flame to dry the surface moisture, carefully place the resin sand core.
With effective degassing to reduce hydrogen, the aluminum liquid is poured into the mold cavity . After cooling, take out the parts, and a beautiful aluminum alloy artwork is displayed in front of us.
By the numerical control hot-box core shooter machine, we can manufacture precision dimensions and high-strength cores, strictly controlling the raw resin sand and the temperature & time parameters of heating. Therefore, the excellent cavity ensures the beautiful surface and good dimensional tolerance of these aluminum products.
After CNC machining, the perfect finished product is successfully made. Especially suitable for manifold and pump or valve components with complex cavities and high pressure requirement.
Our manual molding process is suitable for complex aluminum and copper castings,the mold and casting costs are relatively low and be competitive.
| Product Description | Aluminium Casting and machining side main bracket |
| Actual Part Weight (Kg) | 9.1 |
| Capabilities Applied/Processes | Aluminum sand Casting, Shot Blasting, CNC Machining |
| Equipment Used to Manufacture Part | sand casting machine, Shot blasting machine, HASS CNC Machine |
| Overall Part Dimensions (mm) | 550x360x330 |
| Tightest Tolerances (mm) | 0.02 |
| Material Used | ZL101 Aluminum Alloy |
| Material Finish | Sand blasting |
| In process testing/inspection performed | CMM Inspection |
| Delivery Location | USA |
- Similar Products
$30000.00
1 Piece (MOQ)
Advanced Wheel-Type Sand Mixer for Casting and Ceramics
Qingdao Jinran Machinery Co., Ltd
$15.00
300 Pieces (MOQ)
China Foundry Custom Cast Valve Body Machinery Parts
Sino Industry and Trade Co., Ltd.