Customized Size Monel 404 Nickel Alloy Strip for Marine Fixtures

Price $36.00
Min Order 100 kg
Availability In Stock
Shipping From Tianjin, China
Popularity 313 people viewed
Send Inquiry View Full Page
Model NO.:
Monel 404
Application:
Aviation, Electronics, Industrial, Medical, Chemical
Standard:
JIS, GB, DIN, ASTM, AISI
Purity:
50%
Alloy:
Alloy
Type:
Nickel Strip
Powder:
Not Powder
Thickness:
0.4-8mm
Width:
1000/1219/1500mm
Length:
as Your Requirments
MOQ:
100kgs
Sample:
Free-Sample
Surface:
2b, No.1
Technique:
Cold Rolled, Hot Rolled
Mtc:
En 10204 Type 3.1
Stock:
in Stock
T.S.(≥ MPa):
483
Key Words:
Monel 404 Nickel Price
Trademark:
ZYTC
Transport Package:
Wooden Package
Specification:
Monel 404
Origin:
China
HS Code:
7502200000
Product Description



 

Single-phase solid solution Ni-Cu alloy Monel 404 Nickel Based Plate for Chemistry and petrochemical yield

  

Super Alloy Monel 404

 

Specifications

The following specifications cover Super Alloy Monel 404(tm)

 

  • ASTM F96
  • UNS N04404

Property Results

Chemistry Data : [top]

 

Aluminum

 

0.05 max

Carbon

 

0.15 max

Copper

 

Balance

Iron

 

0.5 max

Manganese

 

0.1 max

Nickel

 

52 - 57

Silicon

 

0.1 max

Sulphur

 

0.024 max

 

 
Principal Design Features This alloy of copper- nickel is another in the Monel family. It has excellent brazing capability and very low magnetic permeability.
 
Applications Used for capsules for transistors, ceramic-to-metal sealing.
 
Machinability Conventional machining techniques used for iron based alloys may be used. This alloy does work-harden during machining and has higher strength and "gumminess" not typical of steels. Heavy duty machining equipment and tooling should be used to minimize chatter or work-hardening of the alloy ahead of the cutting. Most any commercial coolant may be used in the machining operations. Water-base coolants are preferred for high speed operations such as turning, grinding, or milling. Heavy lubricants work best for drilling, tapping, broaching or boring. Turning: Carbide tools are recommended for turning with a continuous cut. High-speed steel tooling should be used for interrupted cuts and for smooth finishing to close tolerance. Tools should have a positive rake angle. Cutting speeds and feeds are in the following ranges: For High-Speed Steel Tools For Carbide Tooling Depth Surface Feed Depth Surface Feed of cut speed in inches of cut speed in inches inches feet/min. per rev. inches feet/min. per rev. 0.250" 60-70 0.030 0.250" 250-300 0.020 0.050" 90-100 0.010 0.050" 300-350 0.008 Drilling: Steady feed rates must be used to avoid work hardening due to dwelling of the drill on the metal. Rigid set-ups are essential with as short a stub drill as feasible. Conventional high-speed steel drills work well. Feeds vary from 0.0007 inch per rev. for holes of less than 1/16" diameter, 0.003 inch per rev. for 1/4" dia., to 0.010 inch per rev. for holes of 7/8"diameter. Surface speeds of 45-55 feet/minute, are best for drilling. Milling: To obtain good accuracy and a smooth finish it is essential to have rigid machines and fixtures and sharp cutting tools. High-speed steel cutters such as M-2 or M-10 work best with cutting speeds of 60 to 80 feet per minute and feed of 0.005"-0.008" per cutting tooth. Grinding: The alloy should be wet ground and aluminum oxide wheels or belts are preferred.
 
Forming This alloy has good ductility and may be readily formed by all conventional methods. Because the alloy is stronger than regular steel it requires more powerful equipment to accomplish forming. Heavy-duty lubricants should be used during cold forming. It is essential to thoroughly clean the part of all traces of lubricant after forming as embrittlement of the alloy may occur at high temperatures if lubricant is left on.
 
Welding The commonly used welding methods work well with this alloy. Matching alloy filler metal should be used. If matching alloy is not available then the nearest alloy richer in the essential chemistry (Ni, Co, Cr, Mo) should be used. All weld beads should be slightly convex. It is not necessary to use preheating. Surfaces to be welded must be clean and free from oil, paint or crayon marking. The cleaned area should extend at least 2" beyond either side of a welded joint. Gas-Tungsten Arc Welding: DC straight polarity (electrode negative) is recommended. Keep as short an arc length as possible and use care to keep the hot end of filler metal always within the protective atmosphere. Shielded Metal-Arc Welding: Electrodes should be kept in dry storage and if moisture has been picked up the electrodes should be baked at 600 F for one hour to insure dryness. Current settings vary from 50 amps for material 0.062" thick up to 190 amps for material of 1/2" and thicker. It is best to weave the the electrode slightly as this alloy weld metal does not tend to spread. Cleaning of slag is done with a wire brush (hand or powered). Complete removal of all slag is very important before successive weld passes and also after final welding. Gas Metal-Arc Welding: Reverse-polarity DC should be used and best results are obtained with the welding gun at 90 degrees to the joint. For Short-Circuiting-Transfer GMAW a typical voltage is 19-25 with a current of 100-175 amps and a wire feed of 225-400 inches per minute. For Spray-Transfer GMAW voltage of 26 to 33 and current in the range of 200-350 amps with wire feed rate of 200-500 inches per minute, depending on filler wire diameter. Submerged-Arc Welding: Matching filler metal, the same as for GMAW, should be used. DC current with either reverse or straight polarity may be used. Convex weld beads are preferred.
 
Heat Treatment The alloy does not respond to heat treatment except for annealing after cold working.
 
Forging No data. However the alloy is forgeable.
 
Hot Working No data, but capable of being hot worked.
 
Cold Working Cold forming may be done using standard tooling although plain carbon tool steels are not recommended for forming as they tend to produce galling. Soft die materials (bronze, zinc alloys, etc.) minimize galling and produce good finishes, but die life is somewhat short. For long production runs the alloy tool steels ( D-2, D-3) and high-speed steels (T-1, M-2, M-10) give good results especially if hard chromium plated to reduce galling. Tooling should be such as to allow for liberal clearances and radii. Heavy duty lubricants should be used to minimize galling in all forming operations. Bending of sheet or plate through 180 degrees is generally limited to a bend radius of 1 T for material up to 1/8" thick and 2 T for material thicker than 1/8".
 
Annealing Anneal at 1400 F for 1 hour.
 
Hardening Hardens due to cold working only.
 

Physical Data : [top]

  
Density (lb / cu. in.)0.322
Specific Gravity8.86
Specific Heat (Btu/lb/Deg F - [32-212 Deg F])0.099
Electrical Resistivity (microhm-cm (at 68 Deg F))300
Melting Point (Deg F)2400
Thermal Conductivity146
Mean Coeff Thermal Expansion7.4
Magnetic Permeability1
Modulus of Elasticity Tension24.5

 


Mechanical Data : [top]

Form

 

Strip

Condition

 

Test Specimen Annealed

Temper

 

70

Tensile Strength

 

65

Yield Strength

 

23

Elongation

 

45

Rockwell

 

B55






 






 

Q1: Do you accept the trial order ?
A1: Yes,if we have the exactly size in stock.we can delivery even 1 piece/meter .

Q2: Can I have free sample before making orders?

A2: Yes,we can supply free sample as requirement,but buyer needs to pay the freight charges ,the freight fee will return to buyer after making order.

Q3: How do you control the quality ?
A3: MTC and PMI will be sent before shipment,any 3rd party inspection if need .

Q4: How about your delivery time ?
A4: Generally delivery time is 15 working days .

Q5: How can I quickly get the price list ?
A5: Directly click "chat now" or send us email with detail specifications,you will get the official price list in 1 hour .


  • Similar Products
Full Page Contact Supplier
↑