Electric Insulation Fiberglass Insulating Banding Tape

Price $1.50
Min Order 1000 Rolls
Availability In Stock
Shipping From Shanghai, China
Popularity 252 people viewed
Send Inquiry View Full Page
Model NO.:
LT-PGW
Application:
Automotive Wiring, Electrical Insulation, HVAC System, Pipe Insulation
Color:
White
Material:
Glass Fiber
Maximum Voltage:
20KV~100KV
Thermal Rating:
H 180
Width:
10mm, 15mm, 20mm, 25mm, 30mm, 32mm, 35mm, 40mm
Thickness:
0.17mm, 0.2mm, 0.25mm, 0.3mm, 0.32mm
Raw Material:
Fiber Glass Yarn + Unsaturated Polyester Rein
Package:
50~200 Meters Per Roll
Thermal Grade:
F, H Grade
Type:
Solid
Chemistry:
Inorganic Insulation
Classification:
Inorganic Insulation Material
Certification:
ISO9001
Brand:
Lontom
Trademark:
LONTOM
Transport Package:
Spool
Specification:
RoHS
Origin:
Shanghai, China
HS Code:
70199000
Product Description


Electric Insulating Edge Banding Tape
1.Thickness:0.2~0.5mm
2.Fiberglass banding tape
3.Self-adhesive insulation tape
4.SGS,RoHS

The banding tapes are of high quality, which consist of parallel twisted E-glass yarns preimpregnated with a special thermosetting polyester resin and manufactured with the proprietory technology and advanced equipments.

It's widely used in AC. DC motors, generators and transformers especially in traction motors.

 Main Properties:

1.Thickness: 0.20mm±10%,0.30mm±10%
 
2.Width: 10mm~50mm±10%
 
3.Length/Spool: 50~200 meters
 
4.Standard color: White

5.Thermal Grade: F grade(155ºC)
               H grade(180ºC)

6.Curing condition (Time to bring the piece to the temperature is not considered)
Temperature ºC160150135120115
Timehour2.5351420
 
7.Storage Stability:
Storage temperatureºC10152030
TimeMonth2015106



Technical Data:

Test contentUnitStandard Value 
Thermal class HF 
Volatile content%≤ 2 
Loss of weight at calcination%26±2 
Soluble resin content%≥ 90 
Tensile strength before curingN/cm≥1500 ≥1000  
Maximum pull while bandingN/cm800800 
Tensile strength of ringlike sample at room temperature after curingMpa20ºC 
above :900 above :900  
Tensile strength of ringlike sample at working temperature after curingMpa180ºC150ºC 
≥600 ≥560  
Proof tracking index ≥500V  
Arc resistanceS≥160 
Breakdown voltage parallel to layersKVnormal condition:≥25
after soaked in water for 24 hours:≥10		 
ThermosettingOK 
Loss of tensile strength after soaked in oil≤10%  
 