HDPE Injection Grade Dow Kt10000ue, Mi=8
| Price | $1250.00 |
|---|---|
| Min Order | 24 Tons |
| Availability | In Stock |
| Shipping From | Shanghai, China |
| Popularity | 492 people viewed |
Model NO.:
KT10000UE
Feature:
Polymer
CAS No.:
9002-88-4
Formula:
(C2 H4)N
Material:
High Density Polyethylene/HDPE
Usage:
General Plastics
Plastic Properties After Heated:
Thermosetting Plastic
Plastic Forming Method:
Film Pressure
Color:
White
Mfr:
8
Trademark:
DOW
Transport Package:
Plastic Bag
Specification:
25kg bag
Origin:
USA
HS Code:
391230
Product Description
Description:
This high molecular weight, hexene copolymer is tailored for blown film applications that require:Toughness and durability; Good processability; Good blending characteristics with HDPE HMW resins.
Applications:
Typical applications for HHM TR-144 include:T-shirt bags; Multi-wall liners; Trash bags.
Packaging:
In 25kg bag, 26-28MT in one 40HQ.
| No. | Properties | Value (SI Units) | Method |
| 01 | Density | 0.946 g/cm3 | ASTM D1505 |
| 02 | Melt Index, Condition 190°C / 2.16 kg | 0.18 g/10 min | ASTM D1238 |
| 03 | Brittleness Temperature, Type A clamp, Type I specimen | <-75°C | ASTM D746 |
| 04 | ESCR, Condition B (100% Igepal), F50 | >1000 hrs | ASTM D1693 |
| 05 | Flexural Modulus, Tangent - 16:1 span:depth, 12.7 mm/min | 1150 MPa | ASTM D790 |
| 06 | Dart Drop (66 cm) | 90 g | ASTM D1709 |
| 07 | Tensile Strength at Yield, 50.8 mm/min MD | 24 MPa | ASTM D882 |
| 08 | Tensile Strength at Yield, 50.8 mm/min TD | 26 MPa | ASTM D882 |
| 09 | Elongation at Break, 50.8 mm/min MD | 480% | ASTM D882 |
| 10 | Elongation at Break, 50.8 mm/min TD | 640% | ASTM D882 |
| 11 | Elmendorf Tear Strength, MD | 19 g | ASTM D1922 |
| 12 | Elmendorf Tear Strength, TD | 270 g | ASTM D1922 |