$150.00
50 Pieces (MOQ)
Alumina Zirconia Carbon Slide Gate Plate
Jinan Xiazhimu New Materials Co., Ltd.
Swipe or use the arrows to view product images.
High Quality Ladle Refractory Slide Gate Plate for Continuous Casting
| Price | Negotiable |
|---|---|
| Min Order | 50 Pieces |
| Availability | In Stock |
| Shipping From | Shandong, China |
| Popularity | 475 people viewed |
Model NO.:
LS70
Feature:
Corrosion Resistance, Good Insulation Performance, Thermal Shock Resistance, Long Time Materials
Production Process:
Sintering Method
Refractoriness (℃):
1580< Refractoriness< 1770
Shape:
Plate
Type:
Refractory Material
Material:
Al-Zr-C
Al2O3 %:
85%
Zro2 %:
2%
C%:
2.5%
B.D(≥g/cm3):
2.9
a.P.P(≤%):
12
C.C.S(≥MPa):
100
Trademark:
XIAZHIMU
Transport Package:
Wooden Case
Origin:
China
HS Code:
69029000
Product Description
Ladle refractory slide gate plate for continuous casting
Slide gate plate is the key part in the slide gate systems. Function is to control the flow rate of molten steel.
The slide plate is exposed to high temperature molten steel repeatedly, especially the cast hole part, the erosion is serious,
this require the slide plates obtaining features of High strength, excellent corrosion resistance, anti-stripping, to ensure no steel leak during pouring process.
Alumina-carbon, alumina-zirconia-carbon, magnesia-alumina-spinel slide gate plates and corundum, alumina-carbon, mullite, magnesia-alumina-spinel upper and down slide nozzles are made of quality materials with phenolic resin binder through pitch impregnation in vacuum and mid temperature treatment. They are classified into high temperature sintered and unburned products. The products have the good thermal stability, erosion resistance to molten steel, corrosion resistance and long service life. They are widely used in 20-300t steel ladles and various tundishes to well control flow rate of molten steel with safety and easy switch.
The features of Slide gate plates:
1. Flatness of sliding surface ≤0.05mm
2. High mechanical strength
3. High resistance to contamination of molten steel and slag
4. Excellent oxidation resistance
5. Good thermal shock stability
The seal protection for slide gates are mainly for upper slide plate and upper nozzle; lower slide plate and lower nozzle. After one or two times of casting, lower slide plate and nozzle must be replaced and re-installed. The sealing materials could be gaskets made of fiber or fireclay. To ensure the high cleanliness of molten steel and the uniformity of internal quality of slab.
Slide gate plate is the key part in the slide gate systems. Function is to control the flow rate of molten steel.
The slide plate is exposed to high temperature molten steel repeatedly, especially the cast hole part, the erosion is serious,
this require the slide plates obtaining features of High strength, excellent corrosion resistance, anti-stripping, to ensure no steel leak during pouring process.
Alumina-carbon, alumina-zirconia-carbon, magnesia-alumina-spinel slide gate plates and corundum, alumina-carbon, mullite, magnesia-alumina-spinel upper and down slide nozzles are made of quality materials with phenolic resin binder through pitch impregnation in vacuum and mid temperature treatment. They are classified into high temperature sintered and unburned products. The products have the good thermal stability, erosion resistance to molten steel, corrosion resistance and long service life. They are widely used in 20-300t steel ladles and various tundishes to well control flow rate of molten steel with safety and easy switch.
| Al2O3(≥%) | ZrO2(≥%) | C(≥%) | B.D(≥g/cm3) | A.P.P(≤%) | C.C.S(≥Mpa) |
| 90 | / | 3 | 2.9 | 10 | 110 |
| 86 | / | 3 | 2.9 | 10 | 100 |
| 70 | / | 3 | |||
| 80 | 3 | 3 | 3.05 | 10 | 80 |
| 80 | 4 | 3 | 3.05 | 9 | 110 |
| 78 | 3 | 4 | 3 | 10 | 110 |
| 78 | 6 | 3 | 3 | 10 | 110 |
| 80 | 6 | 8 | 3.1 | 10 | 110 |
| 80 | 3 | 3 | 3.05 | 10 | 80 |
| 75 | 3 | 10 | 2.95 | 75 | |
| 80 | / | 3 | 2.8 | 14 | / |
| 80 | / | 3 | 2.8 | 14 | / |
The features of Slide gate plates:
1. Flatness of sliding surface ≤0.05mm
2. High mechanical strength
3. High resistance to contamination of molten steel and slag
4. Excellent oxidation resistance
5. Good thermal shock stability
The seal protection for slide gates are mainly for upper slide plate and upper nozzle; lower slide plate and lower nozzle. After one or two times of casting, lower slide plate and nozzle must be replaced and re-installed. The sealing materials could be gaskets made of fiber or fireclay. To ensure the high cleanliness of molten steel and the uniformity of internal quality of slab.
Slide gate plate
Al-Zr-C material (deep burnt)
Al-C material (burnt, unburnt, nitriding treatment)
MgO-Al material
Ladle Nozzle
Alumina Carbon material
MgO-Alumina material
Lower Nozzle
Alumina Carbon material(pressing type)
MgO-Alumina material
High Alumina (casting type)
| Al2O3(≥%) | ZrO2(≥%) | C(≥%) | B.D(≥g/cm3) | A.P.P(≤%) | C.C.S(≥Mpa) |
| 90 | / | 3 | 2.9 | 10 | 110 |
| 86 | / | 3 | 2.9 | 10 | 100 |
| 70 | / | 3 | |||
| 80 | 3 | 3 | 3.05 | 10 | 80 |
| 80 | 4 | 3 | 3.05 | 9 | 110 |
| 78 | 3 | 4 | 3 | 10 | 110 |
| 78 | 6 | 3 | 3 | 10 | 110 |
| 80 | 6 | 8 | 3.1 | 10 | 110 |
| 80 | 3 | 3 | 3.05 | 10 | 80 |
| 75 | 3 | 10 | 2.95 | 75 | |
| 80 | / | 3 | 2.8 | 14 | / |
| 80 | / | 3 | 2.8 | 14 | / |
Equipments:
Friction brick press 400T
Friction brick press 500T
Friction brick press 630T
Friction brick press 1000T
Hydraulic press 630T
Wet grinding machine
The mixing machine
Tunnel kiln...
- Similar Products
Negotiable
50 Pieces (MOQ)
LV 180 Slide Gate Plate for Ladle Bottom Sliding System
Shandong Sinorefractory New Materials Co., Ltd
$90.00
50 Pieces (MOQ)
Pre-Installed Slide Gate Plate and Nozzle
Jinan Xiazhimu New Materials Co., Ltd.