Lead-Acid Battery Cover/Container Sealing Epoxy Resin/Adhesive/Glue/Color Glue
| Price | $8.00 |
|---|---|
| Min Order | 1 kg |
| Availability | In Stock |
| Shipping From | Jiangsu, China |
| Popularity | 367 people viewed |
Model NO.:
HDJ803/852/862
Condition:
New
Application:
Sealing The Lead Acid Battery Cover
After-Sale Service:
Available
Lead Time:
75days
Related Industry:
VRLA Lead Acid Battery
Warranty:
6months
Trademark:
Jinfan
Transport Package:
Standard Export Package
Origin:
Jiangsu, China
Product Description
| Product Technical Data Sheet | |||
| Type | HDJ-803 | ||
| Part A | Part B | ||
| Appearance | yellowish liquid | brown liquid | |
| viscosity(mpa.s) | 900-2000 | 80-150 | |
| 25ºCBrook field | 30/3# | 30/2# | |
| Specific Gravity25ºC | 1.15±0.05 | 1.10±0.05 | |
| Mixing Ratio(by wt.) | 100 | 50 | |
| Pot life 25ºC | 150g | 15-25min | |
| Curing condition | (60±5)ºC*90min | ||
| Lap shear strength | ≥5MPa | ||
| Adhesion for ABS-ABS | |||
| Hardness(shore D) | ≥80HD | ||
| Weight change after | ≤2% | ||
| immerse in H2SO4 | |||
| (d=1.3)(80ºC*24h) | |||
| Product Technical Data Sheet | |||
| Type | HDJ-852 | ||
| Part A | Part B | ||
| Appearance | yellowish liquid | yellowish liquid | |
| viscosity(mpa.s) | 2800-4200 | 80-200 | |
| 25ºCBrook field | 30/3# | 30/2# | |
| Specific Gravity25ºC | 1.13±0.05 | 1.12±0.05 | |
| Mixing Ratio(by wt.) | 100 | 25 | |
| Pot life 25ºC | 150g | 20-30min | |
| Curing condition | (60±5)ºC*90min | ||
| Lap shear strength | ≥4.5MPa | ||
| Adhesion for ABS-ABS | |||
| Hardness(shore D) | ≥78HD | ||
| Weight change after | ≤2.5% | ||
| immerse in H2SO4 | |||
| (d=1.3)(80ºC*24h) | |||
| Product Technical Data Sheet | |||
| Type | HDJ-862 | ||
| Part A | Part B | ||
| Appearance | Black(Red)liquid | brown liquid | |
| viscosity(mpa.s) | 800-2000 | 150-400 | |
| 25ºCBrook field | 30/3# | 30/2# | |
| Specific Gravity25ºC | 1.15±0.05 | 1.10±0.05 | |
| Mixing Ratio(by wt.) | 100 | 50 | |
| Pot life 25ºC | 60g | 12-18min | |
| Curing condition | (60±5)ºC*90min | ||
| Lap shear strength | ≥3.5MPa | ||
| Adhesion for ABS-ABS | |||
| Hardness(shore D) | ≥78HD | ||
| Weight change after | ≤2% | ||
| immerse in H2SO4 | |||
| (d=1.3)(80ºC*24h) | |||
Package:
- Similar Products
$33000.00
1 Set (MOQ)
Advanced Solar Panel Production Line
Tai'an Lishen Machinery Technology Co., Ltd
$50000.00
1 Piece (MOQ)
Stack and Envelop Machine for Battery Plate Group Enveloping
Better Technology Group Limited