Lead-Free Tss Super Shots for Hunting
| Price | $100.00 |
|---|---|
| Min Order | 1 kg |
| Availability | In Stock |
| Shipping From | Heilongjiang, China |
| Popularity | 381 people viewed |
Application:
Industrial, Hunting
Standard:
GB, ASTM
Purity:
85%-97%
Alloy:
Alloy
Shape:
Round
Type:
Tungsten Balls
Content of W (%):
85W-97W
Density:
17.0-18.5g/cm3
Surface:
Polish
Trademark:
Satellite
Transport Package:
Export
Origin:
Mudanjiang City
HS Code:
8101991000
Product Description
Tungsten Heavy TSS Shots
1, Diameter: 2.0-10.0mm
2, Density: 18.0-18.2 g/cm3
3, Composition: W content: 90-95%, W-Ni-Fe
4, Surface: Sintering surface
Why use tungsten alloy shot?
High density, great hardness and resistance to high temperature make tungsten to be one
of the most sought-after materials for shotgun pellets in shooting history.The density of tungsten alloy is about 18g/cm3, only gold, platinum, and a few other rare metals have a similar density. So it is denser than any other shot material including lead, steel or bismuth. To understand how the density factors into performance, let's look at two spheres about the same size, a golf ball and a ping-pong ball.The golf ball is far denser and will fly farther and hit harder. Now reduce that size down two single No.4 pellets,one steel and the other a tungsten alloy. Get the picture? The tungsten will fly farther, hit harder and penetrate deeper. That means more birds, farther out, with fewer cripples. Another unique property of tungsten is that it is nontoxic;it isfrendly to enviorment,so it is safe for people to handle and work with.
•High density
•Easy to handle
•Safe to use
• High melting point
• Small volume
• Excellent hardness
• Super wearing resistance
• High ultimate tensile strength
• High ductility
• High temperature resistance
• Low vapor pressure
Tungsten Alloy Data Sheet
| Type | Density (g/cm³) | Tensile strength (MPa) | Elongation | Hardness (HRC) |
| 85W-10.5Ni-4.5Fe | 15.8-16.0 | 700-1000 | 20-33 | 20-30 |
| 90W-7Ni-3Fe | 16.9-17.1 | 700-1000 | 20-33 | 24-32 |
| 90W-6Ni-4Fe | 16.7-17.0 | 700-1000 | 20-33 | 24-32 |
| 91W-6Ni-3Fe | 17.1-17.3 | 700-1000 | 15-28 | 25-30 |
| 92W-5Ni-3Fe | 17.3-17.5 | 700-1000 | 18-28 | 25-30 |
| 92.5W-5Ni-2.5Fe | 17.4-17.6 | 700-1000 | 25-30 | 25-30 |
| 93W-4Ni-3Fe | 17.5-17.6 | 700-1000 | 15-25 | 26-30 |
| 93W-4.9Ni-2.1Fe | 17.5-17.6 | 700-1000 | 15-25 | 26-30 |
| 93W-5Ni-2Fe | 17.5-17.6 | 700-1000 | 15-25 | 26-30 |
| 95W-3Ni-2Fe | 17.9-18.1 | 700-900 | 8-15 | 25-35 |
| 95W-3.5Ni-1.5Fe | 17.9-18.1 | 700-900 | 8-15 | 25-35 |
| 96W-3Ni-1Fe | 18.2-18.3 | 600-800 | 6-10 | 30-35 |
| 97W-2Ni-1Fe | 18.4-18.5 | 600-800 | 8-14 | 30-35 |
| 98W-1Ni-1Fe | 18.4-18.6 | 500-800 | 5-10 | 30-35 |
| 90W-6Ni-4Cu | 17.0-17.2 | 600-800 | 4-8 | 25-35 |
| 93W-5Ni-2Cu | 17.5-17.6 | 500-600 | 3-5 | 25-35 |
| Physical Property Standards of Tungsten Super Shot | |||||||||
| D18 | D18.5 | ||||||||
| Nominal Tungsten Weight % | 95 | 97 | |||||||
| Density g/cc | 17.75-18.25 | 18.25-18.75 | |||||||
| Harndess Rockwell C , max | 34 | 35 | |||||||
| Ultimate Strength, ksi (mpa), min | 105(724) | 100(689) | |||||||
| 0.2% offset Yield, ksi (mpa), min | 75 (517) | 75(517) | |||||||
| Elongation %, min | 3 | 2 | |||||||
| Tolerances for Dimensions | ± 0.02mm | ± 0.02mm | |||||||
| Surface Roughness, μ m : | 1.6 | 1.6 | |||||||
| ENERGY COMPARISON - #7 & #9 TSS vs. #5 LEAD SHOT | |||||||||
| PENETRATION ENERGY (lb-ft/in^2) | |||||||||
| DENSITY LBS/IN3 | YARDS | ||||||||
| 0 | 10 | 20 | 30 | 40 | 50 | 60 | |||
| #5 LEAD 4% Sb | 0.38868 | 707.7 | 556.9 | 416.0 | 314.5 | 241.3 | 187.6 | 147.1 | |
| #7 TSS 18 g/cc | 0.6503 | 970.2 | 888.1 | 761.4 | 638.6 | 536.1 | 453.0 | 386.2 | |
| #9 TSS 18 g/cc | 0.6503 | 776.1 | 693.3 | 570.7 | 460.8 | 374.4 | 306.0 | 251.0 | |
| VELOCITY (FPS) | |||||||||
| DENSITY LBS/IN3 | YARDS | ||||||||
| 0 | 10 | 20 | 30 | 40 | 50 | 60 | |||
| #5 LEAD 4% Sb | 0.38868 | 1200 | 1065 | 920 | 800 | 701 | 618 | 547 | |
| #7 TSS 18 g/cc | 0.6503 | 1200 | 1148 | 1063 | 974 | 892 | 820 | 757 | |
| #9 TSS 18 g/cc | 0.6503 | 1200 | 1134 | 1029 | 925 | 834 | 753 | 682 | |
| PELLET ENERGY (lb-ft) | |||||||||
| DENSITY LBS/IN3 | YARDS | ||||||||
| 0 | 10 | 20 | 30 | 40 | 50 | 60 | |||
| #5 LEAD 4% Sb | 0.38868 | 8.00 | 6.30 | 4.70 | 3.56 | 2.73 | 2.12 | 1.66 | |
| #7 TSS 18 g/cc | 0.6503 | 7.62 | 6.98 | 5.98 | 5.02 | 4.21 | 3.56 | 3.03 | |
| #9 TSS 18 g/cc | 0.6503 | 3.90 | 3.48 | 2.87 | 2.32 | 1.88 | 1.54 | 1.26 | |