Low Thermal Conductivity Anti-Spalling Refractory Brick
| Price | Negotiable |
|---|---|
| Min Order | 20 Tons |
| Availability | In Stock |
| Shipping From | Shandong, China |
| Popularity | 318 people viewed |
Model NO.:
DDR50
Feature:
Low Thermal Conductivity, Long Time Materials
Refractoriness (℃):
1770< Refractoriness< 2000
Shape:
Brick
Type:
Refractory Material
Material:
Flint Clay, Synthetic Material
Trademark:
Nie
Transport Package:
Export Wooden Pallet
Origin:
China
Product Description
Product Description
Low thermal conductivity of Anti-spalling Brick is one high quality refractory brick for Cement Rotary Kilns,made of Mullite, Synthetic material, Clay.
Characteristics:
1.Outstanding resistance to alkali attack
2.Excellent thermal-shock resistance
3.Outstanding abrasion resistance
4.Low thermal conductivity (230-280ºC)
5.Decreasing the kiln shell load, the mechanical stress on the lining
Application zone:
Calcining furnace, high temperature zone of kiln inlet, tertiary air duct, precalcining zone of cement rotary kiln.
Physical and chemical index
Company Introduction
Luzhong Refractories
A comprehensive refractory service company integrating refractory research, raw material processing, thermotechnical kiln refractory designing, production, sales and service with an annual capacity of over 300,000 tons and currently having the following:
Low thermal conductivity of Anti-spalling Brick is one high quality refractory brick for Cement Rotary Kilns,made of Mullite, Synthetic material, Clay.
Characteristics:
1.Outstanding resistance to alkali attack
2.Excellent thermal-shock resistance
3.Outstanding abrasion resistance
4.Low thermal conductivity (230-280ºC)
5.Decreasing the kiln shell load, the mechanical stress on the lining
Application zone:
Calcining furnace, high temperature zone of kiln inlet, tertiary air duct, precalcining zone of cement rotary kiln.
Physical and chemical index
| chemical composition | UNIT | SPEC | typical | |
| Al2O3 | % | ≤55 | 51~55 | |
| SiO2 | % | 38~42 | ||
| Fe2O3 | % | ≤1.5 | 1.5 | |
| physical properties | UNIT | SPEC | typical | |
| Bulk Density | BD | g/cm3 | ≤2.4 | 2.25~2.35 |
| Apparent Porosity | AP | % | 17 | |
| Thermal Shock Resistance | TSR - in water at 1100 °C | cycle | ≥10 | 10 |
| Refractoriness Under Load | RUL (ta) | °C | ≥1500 | 1500 |
| Thermal Expansion | TE - at 1000 °C | % | 0.7 | |
| Cold Crushing Strength | CCS | MPa | ≥80 | 80 |
| Thermal Conductivity | TC - at 700 °C | W/mK | ≤1.8 | 1.8 |
| Alkali Resistance | 1100 °C*5h | First grade | ||
Company Introduction
Luzhong Refractories
A comprehensive refractory service company integrating refractory research, raw material processing, thermotechnical kiln refractory designing, production, sales and service with an annual capacity of over 300,000 tons and currently having the following:
- National research institute: National and Local Joint Refractory Engineering Research Centre;
- Refractory base: Zibo Luzhong Refractories Co., Ltd., Xinjiang Tianshan Mountains Refractories Co., Ltd.;
- Special industrial ceramic base: Shandong Shengchuan Ceramics Co., Ltd., Ningxia Shengchuan New Material Co., Ltd.
- New materials base: Shandong Shengchuan New Material Science and Technology Inc.
- Raw material base: Yangquan Luzhong Refractories Co., Ltd., Zibo Langfeng High Temperature Material Co., Ltd.;