Magnesia Hercynite Spinel Refractory Brick-Mtl-I
| Price | $1250.00 |
|---|---|
| Min Order | 20 Tons |
| Availability | In Stock |
| Shipping From | Shandong, China |
| Popularity | 444 people viewed |
Model NO.:
MTL-I
Refractoriness (℃):
1770< Refractoriness< 2000
Feature:
Long Time Materials
Type:
Refractory Material
Shape:
Brick
Trademark:
Nie
Transport Package:
Export Wooden Pallet
Origin:
China
Product Description
Description:
Luzhong Magnesia hercynite Spinel bricks are new developed chrome-free refractories for Cement Rotary Kilns, with excellent performance,our products have been wide used in the domestic and overseas cement projects.
Characteristics:
1.Excellent formation of uniform and stable coating
2.Outstanding thermal-shock resistance
3.Excellent resistance to chemical attack
4.Low thermal conductivity (230-280ºC)
Application:
Sintering zone of cement rotary kiln.
Raw Material:
1.Top grade sintered magnesia;
2.High-purity sintered iron alumina spinel (hercynite)
Physical and chemical index
Product application:
Package:
Luzhong Magnesia hercynite Spinel bricks are new developed chrome-free refractories for Cement Rotary Kilns, with excellent performance,our products have been wide used in the domestic and overseas cement projects.
Characteristics:
1.Excellent formation of uniform and stable coating
2.Outstanding thermal-shock resistance
3.Excellent resistance to chemical attack
4.Low thermal conductivity (230-280ºC)
Application:
Sintering zone of cement rotary kiln.
Raw Material:
1.Top grade sintered magnesia;
2.High-purity sintered iron alumina spinel (hercynite)
Physical and chemical index
| Chemical composition | UNIT | SPEC | Typical | |
| MgO | % | ≥85 | 85~88 | |
| Al2O3 | % | ≥4 | 4~6 | |
| SiO2 | % | 0.8 | ||
| Fe2O3 | % | ≥4 | 4~6 | |
| CaO | % | 1.3 | ||
| Physical properties | UNIT | SPEC | Typical | |
| Bulk Density | BD | g/cm3 | ≥2.9 | 2.9~2.95 |
| Apparent Porosity | AP | % | ≤18 | 17 |
| Thermal Shock Resistance | TSR - in air at 950 °C | cycle | ≥95 | 100 |
| Refractoriness Under Load | RUL (ta) | °C | ≥1650 | 1650-1700 |
| Thermal Expansion | TE - at 1000 °C | % | 1.2 | |
| Cold Crushing Strength | CCS | MPa | ≥50 | 60 |
| Thermal Conductivity | TC - at 700 °C | W/mK | ≤3.5 | 3.5 |
| Note: The above datas are the representative average value measured in accordance with the test methods for general purpose and vary with the fluctuations of normal production conditions.These datas are provided as a technical service,sometimes may be adjusted, so they should not be regarded as the product index. | ||||
Product application:
Package:
- Similar Products
Negotiable
20 Tons (MOQ)
Standard Grade Magnesia Spinel Brick-Sgmtl-I
Zibo Luzhong Refractory Co., Ltd.
Negotiable
20 Tons (MOQ)
Low Thermal Conductivity Magnesia Alumina Spinel Brick-Ddrml-80
Zibo Luzhong Refractory Co., Ltd.
Negotiable
20 Tons (MOQ)
B622 B322 Vdz and ISO Refractory Bricks for Cement Kiln Transition Zone
Zibo Luzhong Refractory Co., Ltd.
$500.00
500 Pieces (MOQ)
Burnt Magnesia Chrome Bricks
Shandong Western Coast Advanced Materials Co., Ltd.