Renz30 Good Elasticity PU Adhesive and Sealant for Car Manufacturer
| Price | $4.00 |
|---|---|
| Min Order | 3000 Pieces |
| Availability | In Stock |
| Shipping From | Guangdong, China |
| Popularity | 269 people viewed |
Model NO.:
renz30
CAS No.:
Reference to MSDS
Bonding Function:
Instant Adhesive
Application:
Automobile
Material:
Polyurethane
Main Agent Composition:
Polyurethane Elastomer
Characteristic:
Weatherability
Promoter Composition:
Complexing Agent
Color:
Black
Origin:
China
Product Description
Fast Drave Away Polyurethane Windshield Adhesive Renz30A
30 High strength polyurethane windshield adhesive
Areas of Application:
Suitable for windshield and side&back window glass bonding
Product features:
High viscosity,excellent initial bonding strength,quickly immobilize the windshield.
High strength and elasticity.
Environment friendly,solvent-free.
Excellent bonding performance.
OEM approved quality.
Four options for primer/ Primerless with different bonding strength.
RENZ 30 Technical Data
Testing Items(2) | Performance |
Appearance | Black homogeneous paste |
Density (g/cm³) | / |
Sagging properties(mm) | 0 |
Shore A-hardness(A°) | 55 |
Tensile strength( Mpa) | 6.5 |
Elongation at break (%) | 450 |
Non-Volatile content (%) | 99 |
Tensile-shear strength(Mpa) | 4.0 |
Tack Free time (min) | 25 |
Curing speed (mm/d) | 3.2 |
Extrudability (g/15s) | 60 |
Pollution properties | Non |
Application temperature (ºC) | -40~90 |
Shelf life(month) (3) | ≥9 |
30 High strength polyurethane windshield adhesive
Areas of Application:
Suitable for windshield and side&back window glass bonding
Product features:
High viscosity,excellent initial bonding strength,quickly immobilize the windshield.
High strength and elasticity.
Environment friendly,solvent-free.
Excellent bonding performance.
OEM approved quality.
Four options for primer/ Primerless with different bonding strength.