Senior Standard Stable Economic Ceramic Rb Silicon Carbide Bricks
| Price | $11.00 |
|---|---|
| Min Order | 1 Piece |
| Availability | In Stock |
| Shipping From | Shandong, China |
| Popularity | 497 people viewed |
Model NO.:
RBSIC
Density:
3.05
Application:
Structure Ceramic, Industrial Ceramic
Type:
Ceramic Plates
Temperature of Application:
1380c
Open Porosity:
0.1
Bending Strength -a:
250 (20c)
Bending Strength -B:
280 (1200c )
Modulus of Elasticity-at Gpa:
330(20c)
Modulus of Elasticity -B:
300 ( 1200c )
Thermal Conductivity:
160;45 (1200c )
Coefficient of Thermal Expansion:
4.5
Rigidity:
13
Acid-Proof Alkaline:
160;Excellent
Color:
Black
Size:
Customized Size
Steel:
Sisic Lined Steel Pipe
Thickness:
6-25mm
Material:
Silicon Carbide
Trademark:
firstar
Transport Package:
Wood Carton
Origin:
China
HS Code:
6909120090
Product Description
Silicon carbide Tiles
Reaction bonded silicon carbide is a multi-phased material typically containing 7-15% silicon metal, some minor amount of unreacted carbon, with the remaining body being SiC. Reaction bonded SiC materials are manufactured utilizing a variety of processes depending on desired final product geometry, configuration, and required tolerances.
Reaction bonded silicon carbide has proven to be an excellent material choice for wear applications such as pipe liners, flow control chokes and larger wear components in the mining as well as other industries. CALSIC RB offers an economical and reliable material option for many applications where the corrosion resistance or wear resistance of CALSIC S (sintered silicon carbide) is not necessary.
Typical properties of silicon carbide are:
Excellent thermal shock resistance
Excellent hot strength
Excellent abrasion resistance
Good thermal conductivity
Relatively low coefficient of thermal expansion
Physical Property:
| No. | Item | SISIC | SSIC | HPSIC | SI3N4SIC | RSIC | ||
| 1 | Max. Temperature(ºC) | ≥1380 | 1600 | SSIC-B | SSIC-C | 1450 | 1650 | |
| 2 | SiC(%) | ≥83-85 | 98 | 98 | 98 | 68 | 100 | |
| 3 | free-Si(%) | <14 | 2 | 2 | 2 | Si3N4 -27% | 0-2 | |
| 4 | Density (g/cm³) | ≥3.02 | 3.08 | 3.20 | 2.65 | 3.15 | 2.75-2.85 | 2.65 |
| 5 | Porosity (%) | ≤0.1 | 11 | 10.8-15.8 | ||||
| 6 | Bending Strength at 20ºC(MPa) | 250 | 400 | 500 | 15 | 550 | 160-170 | 52-72.6 |
| 7 | Bending strength at 1200ºC(MPa) | 280 | 2200 | 2200 | 170-180 | 58-65.7 | ||
| 8 | Elastic Modulus at 20ºC(GPa) | 330 | 400 | 420 | 120 | 420 | 151-208 | |
| 9 | Elastic Modulus at 1200ºC(GPa) | 300 | 410 | 430 | ||||
| 10 | Thermal Conductivity at 1200ºC W/(m·K) | 45 | 90-110 | 60 | 120 | 4.0 | 4.7 | 17.5 |
| 11 | Thermal Expansion (k-1×10-6) | 4.5 | 4.0 | 4.2 | 3.0 | 120 | 4 | 4.7 |
| 12 | Vickers hardness | 2000 | 2000 | 2200 | 1500 | 2500 | ||
Typical applications for silicon carbide are:
Kiln furniture for powder metal and ceramic processing
Kiln components including:
--hearths
--entrance tiles
--skid rails
--muffles
--side walls
--arches
Available Shape and sizes:
Thickness: from 6mm up to 25mm
Regular Shape: SiSiC tiles, SiSiC Pipe tiles, SiSiC Three Links, SiSiC Elbow, SiSiC Cone Cyclone.
Remark: Other sizes and shape are available upon requests.
Packaging:
In carton box, packed in fumigated wooden pallet with net weight 20-24MT/20′FCL.
FAQ
Q: What is your experience in your products?
A: We have 22 years experience in this industry line. We are professional manufacturer in this area.
Q: What is your MOQ?
A: The MOQ is different as per different products, for example, 1 Ton for ceramic ball.
Q: Can you accept small quantity sample order before production?
A: Yes, we can offer sample for your testing first.
Q: Can you provide free sample?
A: Yes, within 1kg.
Q: What is your production time?
A: We have large stock for standard products. Normally within 7-10days after receipt the deposit.
Q: What are your payment terms?
A: T/T, L/C, Western Union
- Similar Products
$10.00
100 gram (MOQ)
Mxene Ti3c2 Powder Titanium Carbide CAS 12363-89-2
Shanghai Epoch Material Co., Ltd.