Product Description
HEBEI YUSEN METAL WIRE MESH CO., LTD.
PROFESSIONAL MANUFACTURER ON STEEL FIBERS
STEEL FIBER FOR CONCRETE REINFORENCEMENT
STEEL FIRBRE, HOOKED ENDS STEEL FIBERS,WAVED STEEL FIBER,MICRO STEEL FIBER,STAINLESS STEEL FIBER.
Steel Fiber With Two Hooked Ends:
Wave Steel Fiber(Mill Cut Steel Fiber)
Length:30-50mm
Tensile Strength: ≥380-1500Mpa
Diameter:0.4-1.0mm
Micro Steel Fiber:
Diameter is between 0.2mm to 0.25mm.
Length is 13mm.
Tensile Strength is >2850MPa.
Stainless steel fiber.
Length:20mm, 25mm, 30mm, 35mm
Diameter:0.3-0.4mm,0.4-0.5mm, 0.45-0.55mm, 0.55-0.6mm
Material:330, 310, 316, 316L, 321, 304, 446, 430, 430AL
Melting point: 1400-1425ºC, 1400-1450ºC,, 1425-1510ºC,, 1500-1580ºC
Glued steel fiber
Dia: 0.5-0.95mm
Length: 30-60mm
Tensile strength: >1100MPa
2.Usage:
It is widely used in the fields of buildings,road surface,bridges,tunnels,airport road surface,water conservancy projects,military engineering,and all kinds of building products
3.How to use it?
1.invest blender stir about 30 second steel fiber and thick aggregate first, make the steel fiber disperse among the stones, it is unlikely to form the group.
2.Put sand and cement into blender do, stir 30 second 3 and then with water among the mixer rotating again, make the machine stired again.
3.Fen plants left and right sides.
4.Advantage:
1.Improve refractories performance
2.Improve refractories longevity
3.Improve refractories durability
4.reduce furnace downtime and maintainace cost
5. Packing:
20KG/Carton , 20KG/Bag , or according to your requirement
PROFESSIONAL MANUFACTURER ON STEEL FIBERS
STEEL FIBER FOR CONCRETE REINFORENCEMENT
STEEL FIRBRE, HOOKED ENDS STEEL FIBERS,WAVED STEEL FIBER,MICRO STEEL FIBER,STAINLESS STEEL FIBER.
Steel Fiber With Two Hooked Ends:
Size | Diameter (mm) | Length (mm) | Proportion (mm) | Tensile strength (MPa) |
| YS1.05-50 | 1.05 | 50 | 48 | ≥1000 |
| YS0.9-50 | 0.9 | 50 | 55 | ≥1000 |
| YS0.9-40 | 0.9 | 40 | 45 | ≥1000 |
| YS0.8-50 | 0.8 | 50 | 62 | ≥1000 |
| YS0.7-35 | 0.7 | 35 | 50 | ≥1000 |
| YS0.6-35 | 0.6 | 35 | 58 | ≥1000 |
| YS0.6-30 | 0.6 | 30 | 50 | ≥1000 |
| YS0.6-25 | 0.6 | 25 | 42 | ≥1000 |
| YS0.5-25 | 0.5 | 25 | 50 | ≥1000 |
Wave Steel Fiber(Mill Cut Steel Fiber)
Length:30-50mm
Tensile Strength: ≥380-1500Mpa
Diameter:0.4-1.0mm
Micro Steel Fiber:
Diameter is between 0.2mm to 0.25mm.
Length is 13mm.
Tensile Strength is >2850MPa.
Stainless steel fiber.
Length:20mm, 25mm, 30mm, 35mm
Diameter:0.3-0.4mm,0.4-0.5mm, 0.45-0.55mm, 0.55-0.6mm
Material:330, 310, 316, 316L, 321, 304, 446, 430, 430AL
Melting point: 1400-1425ºC, 1400-1450ºC,, 1425-1510ºC,, 1500-1580ºC
Glued steel fiber
Dia: 0.5-0.95mm
Length: 30-60mm
Tensile strength: >1100MPa
2.Usage:
It is widely used in the fields of buildings,road surface,bridges,tunnels,airport road surface,water conservancy projects,military engineering,and all kinds of building products
3.How to use it?
1.invest blender stir about 30 second steel fiber and thick aggregate first, make the steel fiber disperse among the stones, it is unlikely to form the group.
2.Put sand and cement into blender do, stir 30 second 3 and then with water among the mixer rotating again, make the machine stired again.
3.Fen plants left and right sides.
4.Advantage:
1.Improve refractories performance
2.Improve refractories longevity
3.Improve refractories durability
4.reduce furnace downtime and maintainace cost