Audited Supplier
CL-PVDF
Electrical Winding Insulation, Hybrid Insulation
OEM
-55-150 Degrees
Insulation Sleeve & Tube
Hybrid Insulation Materials
Iatf 16949
Carton
Customizable
Changzhou
Product Description
Basic information
Shrink ratio: 2:1
Semi-rigid, very thin wall insulation
Excellent flammability
High temperature resistant to 175ºC
Good toughness, excellent abrasion resistance, physical and chemical properties.
ROHS and REACH compliant
Operating temperature: -55ºC ~ 150ºC
Minimum shrink temperature: 155ºC
Minimum fully recovery temperature: 175ºC
UL224 E360866 150ºC 600V VW-1
Product Description
Other sizes are available upon request.
Shrink ratio: 2:1
Semi-rigid, very thin wall insulation
Excellent flammability
High temperature resistant to 175ºC
Good toughness, excellent abrasion resistance, physical and chemical properties.
ROHS and REACH compliant
Operating temperature: -55ºC ~ 150ºC
Minimum shrink temperature: 155ºC
Minimum fully recovery temperature: 175ºC
UL224 E360866 150ºC 600V VW-1
| Application: | Insulators, Electrical Winding Insulation, Winding Wire Coating Insulation, Electrical Base, Shell, Connector |
| Type: | Insulation Sleeve |
| Chemistry: | Hybrid Insulation |
| Material: | Special Fluoropolymer |
| Thermal Rating: | 175degrees |
| Shrink ratio: | 2:1 |
| Maximum Voltage: | >100KV |
| Property | Test method | Soft (150 ° C) typical | Soft (175 ° C) typical |
| Tensile strength | ASTM D2671 | ≥24.5M Pa | ≥34.5M Pa |
| Ultimate elongation | ASTM D2671 | ≥150% | ≥150% |
| Ultimate elongation after aging | 225ºC,168h | ≥100% | ≥100% |
| Heat shock | 275ºC,4h | No dripping, no cracking | No dripping, no cracking |
| Cold bend | -55ºC,4h | No cracking | No cracking |
| Dielectric | ASTM D2671 | ≥15.7kV/mm | ≥31.5kV/mm |
| Volume resistivity | ASTM D257 | ≥1013Ω.cm | ≥1013Ω.cm |
| Flammability | UL-224 | VW-1 | VW-1 |
Product Description
CL-PVDF is made of special irradiation cross-linked fluoropolymer PVDF with outstanding chemical and solvent resistance and high-temperature performance. It is tough, semi-rigid, very thin wall especially suitable for applications requiring high-temperature performance, outstanding abrasion resistance and cut-through resistance, or superior chemical and solvent properties. It is also used for insulation and strain relief of soldered joints, identification and inspection of covered components.
| size | As supplied(mm) | After recovered(mm) | Standard packing | ||
| inch | mm | Inside diameter(min) | Inside diameter(max) | Wall thickness | (m/pc,m/roll) |
| 3/64 | 1.2 | 1.2 | 0.6 | 0.25+0.05 | 1.2/200 |
| 1/16 | 1.6 | 1.6 | 0.8 | 0.25+0.05 | 1.2/200 |
| 3/32 | 2.4 | 2.4 | 1.2 | 0.25+0.05 | 1.2/200 |
| 1/8 | 3.2 | 3.2 | 1.6 | 0.25+0.05 | 1.2/200 |
| 3/16 | 4.8 | 4.8 | 2.4 | 0.25+0.05 | 1.2/100 |
| 1/4 | 6.4 | 6.4 | 3.2 | 0.30+0.08 | 1.2/100 |
| 3/8 | 9.5 | 9.5 | 4.8 | 0.30+0.08 | 1.2/100 |
| 1/2 | 12.7 | 12.7 | 6.4 | 0.30+0.08 | 1.2/100 |
| 3/4 | 19.1 | 19.1 | 9.5 | 0.43+0.08 | 1.2/50 |
| 1 | 25.4 | 25.4 | 12.7 | 0.48+0.08 | 1.2/50 |