Product Description
Molybdenum disilicide(MoSi2) heating element/heater:
Mosi heating element is a kind of resistance heating element basically made of pure molybdenum Disilicide. In oxidizing atmosphere, a layer of compact quartz protective film is formed on the surface of Mosi 2 element owing to the high temperature combustion, which prevents Mosi 2 from continuously oxidizing.
In oxidizing atmosphere, its Max temperature can reach 1800 c and its applicable temperature is 500-1700. It can be widely used in such applications as sintering and heat treatment of ceramics, magnet, glass, metallurgy, refractory etc. the commercial name of our Mosi 2 heating element is KERONE Mosi 2 Heating Element.
Molybdenum disilicide(MoSi2) heating element/heater:
1. According to temperature: 1700C 1800C 1900C
2. According to Shape: U, W, I, U type L shape, W type L shape, Spiral types.
Molybdenum disilicide(MoSi2) heating element/heater standard size
M1700 type (D1/D2): dia3/6, dia4/9, dia6/12, dia9/18, dia12/24
M1800 type (D1/D2): dia3/6, dia4/9, dia6/12, dia9/18, dia12/24
M1900 type (D1/D2): dia3/6, dia4/9, dia6/12, dia9/18, dia12/24
Chemistry Character
MoSi2 heating element is used in the high temperature under oxidizing atmosphere. It will form the SiO2 film which can keep the element from being melted. During the oxidizing process, the SiO2 protecting film is formed again when the element continues to be used. The MoSi2 heating element must not be used in the temperature between 400C and 700C for a long time, otherwise the element will be cremated under the strong oxidizing function in the low temperature.
Recommend surface load:
The influence of operation temperature on the heater surface in a different atmosphere:
2. According to Shape: U, W, I, U type L shape, W type L shape, Spiral types.
Molybdenum disilicide(MoSi2) heating element/heater standard size
M1700 type (D1/D2): dia3/6, dia4/9, dia6/12, dia9/18, dia12/24
M1800 type (D1/D2): dia3/6, dia4/9, dia6/12, dia9/18, dia12/24
M1900 type (D1/D2): dia3/6, dia4/9, dia6/12, dia9/18, dia12/24
Chemistry Character
MoSi2 heating element is used in the high temperature under oxidizing atmosphere. It will form the SiO2 film which can keep the element from being melted. During the oxidizing process, the SiO2 protecting film is formed again when the element continues to be used. The MoSi2 heating element must not be used in the temperature between 400C and 700C for a long time, otherwise the element will be cremated under the strong oxidizing function in the low temperature.
Physics characters of Molybdenum disilicide(MoSi2) heating element/heater:
| Bulk density | Bending strength | Hardness | Apparent porosity | Drawing water rate | Thermal elongation |
| 5.5~5.6g/cm3 | 20MPa(20ºC) | (hv)570kg/mm² | 0.5~2.0% | 0.5~2.0% | 4% |
Recommend surface load:
| Furnace Temp(°c) | 1400 | 1500 | 1600 | 1650 | 1700 |
| Surface load of hot zone(W/cm²) | <18 | <15 | <12 | <10 | <8 |
The influence of operation temperature on the heater surface in a different atmosphere:
Atmosphere | The Maximum Using Temperature of Elements | |
1700 | 1800 | |
No2 ,Co2 ,O2 ,Air | 1700°C | 1800°C |
He ,Ar ,Ne | 1650°C | 1750°C |
So2 | 1600°C | 1700°C |
CO ,H2 | 1500°C | 1600°C |
Wet H2 | 1400°C | 1500°C |
Dry H2 | 1350°C | 1450°C |
When you place order, plz inform us below data:
Material Grade: 1700C / 1800C / 1900C
Diameter: D1/D2, mm
Hot zone length: Le, mm
Cold zone length: Lu, mm
Shank Space: A, mm
Order Sample: diaD1/D2 x Le x Lu x A
Material Grade: 1700C / 1800C / 1900C
Diameter: D1/D2, mm
Hot zone length: Le, mm
Cold zone length: Lu, mm
Shank Space: A, mm
Order Sample: diaD1/D2 x Le x Lu x A
1. We provide special designed Molybdenum Disilicide (MoSi2) heating element according to customer needs, enabling an optimized element design for each particular application.
2. Delivery time: 7days after receipt deposit.
3. Package: Synthetic Wooden Box with Cardboard Box and sponge
We also received OEM service; the package can be designed according to your requirements.
1. Timely response,
Timely response to your inquiry, multiple choice recommendations based on your demand, quickly respond mails and provide solutions.
2. Sample evaluation
Sample and trial order is accepted for the quality evaluation.
3. Strict quality control
Arrange production on time and control quality strictly.
4. Shorter delivery time.
Book the earliest vessel or plane to guarantee the delivery time.
5. Professional Services
Provide all the detailed news and pictures from order to delivery;
Offer relative export documents and original certificate if needed;
Warm and considerable after-sale service
We also received OEM service; the package can be designed according to your requirements.
Shipping: By vessel or by plane from any Chinese port, Samples can be delivered by International express.