Audited Supplier
5J1580
GB
Cold Drawn
Strip, Roll
Polished
Exhaust Thermometers
(0.05-3.0mm)T*(>1mm)W
Bright,Printed
Can Replace Kanthal 155
Ni20mn6
Ni36
8.1g/cm3
Medium Sensitivity, Medium Resistance, Medium Temp
UALLOY
Rolled, Then Packed Into Plywood Pallet or Case
(0.06-3.0)mm*(1-150)mm
Hangzhou, China
722699900
Product Description
5J1580 Thermal Bimetal Strip
Similar marks in different country
Chinese mark:5J1580/5J16
German mark:TB1577
American mark:ASTM B388 TM-1
Description
Thermal bimetallic layer is composed of two layers with different linear Solid combination of expansion coefficient of metal composite materials.It holds the higher thermal sensitivity and high resistivity, low temperature stability is good, the welding is more easily and widely used. And it mainly is used for temperature measurement and automatic control equipment in the thermal sensitive element.
Component laminations and Chemical content
High expansive lamination(Active):Ni20Mn6
Low expensive lamination(Passive):Ni36
Chemical composition(%)
| Grade | C | Si | Mn | P | S | Ni | Cr | Cu | Fe |
| Ni36 | ≤0.05 | ≤0.3 | ≤0.6 | ≤0.02 | ≤0.02 | 35~37 | - | - | Bal. |
| Grade | C | Si | Mn | P | S | Ni | Cr | Cu | Fe |
| Ni20Mn6 | ≤0.05 | 0.15~0.3 | 5.5~6.5 | ≤0.02 | ≤0.02 | 19~21 | - | - | Bal. |
Typical Physical properties
| Density (g/cm3) | 8.1 |
| Electrical resistivity at 20ºC(ohm.mm2/m) | 0.8±5% |
| Thermal conductivity, λ/ W/(m*ºC) | 12 |
| Elastic Modulus, E/ Gpa | 147~177 |
| Bending K / 10-6 ºC-1(20~135ºC) | 15 |
| Temperature bending rate F/(20~130ºC)10-6ºC-1 | 28.5%±5% |
| Allowable temperature (ºC) | -70~ 350 |
| Linear temperature (ºC) | -20~ 180 |
Application
The material is mainly in automatic control devices and instrumentation (eg: exhaust thermometers, thermostats, voltage regulators, temperature relay, automatic protection switching, diaphragm meters, etc.) make temperature control, temperature compensation, current limit, temperature indicator and other heat-sensitive components.
Feature
The basic characteristics of Thermostat Bimetallic is bending deformation with temperature changes, resulting in a certain moment.
Thermostat Bimetallic Strip expansion coefficient is different from the two or more layers of metal or alloy along the entire contact surface firmly bonded, having a temperature-dependent shape change occurs thermosensitive functional composites. Wherein the higher expansion coefficient of the active layer is a layer called a low coefficient of expansion of the layer is named passive layer.
Style of supply
| Alloys Name | Type | Dimension | ||
| OhmAlloy-5J1480 | Strip | W= 1~150mm | T= 0.05-3.0mm | |