Ceramic Tube
Custiomized
6, 8, 12 Inches
15um 30um 50um 100um
Light Brown, Brown, Blue-Gray,
Moulding
2.3-2.5 g/cm3
Corrosion Resistance, Have Pore Size
40%, 50% or Customized
Alumina Ceramic
Hra ≥ 50
MPa ≥ 40
MPa≥600
40%
+/-0.10 mm
+/-0.10 mm
Ra 0.8-1.6
Innovacera
Carton Package
Customized
Fujian, China
Product Description
The range of Innovacera porous ceramic filters are made from aluminum oxide and silicon carbide. The strong, uniform porous
ceramic has 40-50% open porosity with a tortuous pore structure and is available in pore sizes ranging from 1 to 120 microns.
Monolithic, single grade, aluminum oxide porous ceramic is available in 1, 15, 30, 50, 60, 80, 100 and 120 micron pore sizes.
Aluminum oxide is the most standard material, with a density of 2.2 g/cc, and has a maximum operating temperature of 1400 °F
(800 °C).
The range of porous ceramic products includes:
• Membrane and monolithic tubes
• Discs
• Plates and other components made from aluminum oxide and silicon carbide where tightly controlled pore size and porosity is
critical.
Porous Ceramics Applications
• Used in tough applications to replace porous metal or as an alternative to plastic or fabric media
• Cleaned and reused using a variety of methods depending on the contaminant to be removed
ceramic has 40-50% open porosity with a tortuous pore structure and is available in pore sizes ranging from 1 to 120 microns.
Monolithic, single grade, aluminum oxide porous ceramic is available in 1, 15, 30, 50, 60, 80, 100 and 120 micron pore sizes.
Aluminum oxide is the most standard material, with a density of 2.2 g/cc, and has a maximum operating temperature of 1400 °F
(800 °C).
The range of porous ceramic products includes:
• Membrane and monolithic tubes
• Discs
• Plates and other components made from aluminum oxide and silicon carbide where tightly controlled pore size and porosity is
critical.
Specifically tailored techniques include:
• Spraying
• Brushing
• Backwashing
• Oven firing
• Dilute acid cleaning
• Solvent cleaning plus steam
• Ultrasonic cleaning
• Spraying
• Brushing
• Backwashing
• Oven firing
• Dilute acid cleaning
• Solvent cleaning plus steam
• Ultrasonic cleaning
Porous Ceramics Applications
• Used in tough applications to replace porous metal or as an alternative to plastic or fabric media
• Cleaned and reused using a variety of methods depending on the contaminant to be removed
Applications
• Used in tough applications to replace porous metal or as an
alternative to plastic or fabric media
• Cleaned and reused using a variety of methods depending
on the contaminant to be removed
• Filters for gases and liquids
• Capillary Electrophoresis
• Filtration for heavy metal ions (Cr, Ni etc) in water
• High temperature chemical support for gas absorption
• High efficiency flow through catalytic supports
• Gas burners
• Chromatography
• Micro trapping systems and bio-catalytic supports
• Vacuum holding plates (vacuum chunk)
• Nano-membrane supports for sensor applications
• Micro-bubble diffusers
• Fine or micro channels for electrophoresis
• Chemical or bio reactor
• Used in tough applications to replace porous metal or as an
alternative to plastic or fabric media
• Cleaned and reused using a variety of methods depending
on the contaminant to be removed
• Filters for gases and liquids
• Capillary Electrophoresis
• Filtration for heavy metal ions (Cr, Ni etc) in water
• High temperature chemical support for gas absorption
• High efficiency flow through catalytic supports
• Gas burners
• Chromatography
• Micro trapping systems and bio-catalytic supports
• Vacuum holding plates (vacuum chunk)
• Nano-membrane supports for sensor applications
• Micro-bubble diffusers
• Fine or micro channels for electrophoresis
• Chemical or bio reactor
Alumina materials properties
---
| Properties | Unit | Pore Ceramic |
| Al2O3 Content | wt% | ≥ 80 |
| SiO2 Content | wt% | 16-18 |
| Density | g /cm3 | 2.3-2.5 |
| Hardness (HRA) | HRA ≥ | 50 |
| Flexure strength | MPa ≥ | 40 |
| Compressive Strength | MPa≥ | 600 |
| Porosity Factor | % | 40 |
| Work Pressure | MPa ≤ | 10 |
| Acid Resistance | mg/cm2 ≤ | 10 |
| Alkali Resistance | mg/cm2 ≤ | 20 |