XGPF1206
Filling Material, Resin Reinforcement
PARA Aramid
Abrasion-Resistant, Flame Retardant, Anti-Distortion, Heat-Resistant
Chopped Strands
Yellow
High Strength Fiber
Synthetic Fiber
1.47g/cm3
1.5D
6mm
12um
19.4cn/Dtex
89gpa
2.8%
>450
4%
1414
XIANGU
10kg/Carton
6mm
China
5402119000
Product Description
6mm Kevlar Chopped Strands for Audio Speaker Paper was chopped in 6mm by a special cutting machine.This fiber has high strength and modulus,strong hydrogen bonding strength,strength up to 28 g/d or more,strength is 5-6 times of steel wire.specific modulus 2-3 times of it,toughness 2 times of it while weight is just 1/5 of the wire.Continuous using temperature range is extremely wide,long running in the range of -196 ºC to 204 ºC,no decomposition and melting at high temperature of 560 ºC,strength can maintain 75% through 100 hours at 200 ºC,also has good chemical solvent resistance,resisting acid and alkali, anti-aging,good adhesion to rubber.Usually it is used as a reinforcing material in the fields of thermoplastics,thermosetting plastics,rubber,silica gel,high-temperature composite structures,brake pads,clutch linings,friction material,wear-resistant filler,cable sheathing,gaskets,slot insulation,phase insulation barrier,interturn insulation and so on.
SPECIFICATIONS:
| Model: | XGPF1206 |
| Color: | yellowish |
| Fiber type: | Para-aramid |
| Density(g/cc) | 1.47 |
| Linear density of mono filament(D) | 1.5 |
| Filament diameter(μm) | 12 |
| Fiber length(mm) | 6.0 |
| Tensile strength( cN/dtex) | 19.4-21 |
| Elongation at break(%) | 2.5-3.84 |
| Tensile modulus(GPa) | 80~120 |
| Shrinkage(%) | <0.2(190ºC×15m) |
| Moisture (%): | <0.2 |
APPLICATION FIELDS:
1.Paper cone reinforcement material:Loudspeaker paper cone,audio speaker paper, audio diaphragm,Horn Cone.
2.Engineering Plastics,thermosetting resin,friction materials,automotive brakes,composite materials and Kevlar reinforced paper.
3.reinforcing materials,construction,rubber,reinforced cable,cable and other high-intensity rope.
4.composite material with resin or rubber,can significantly reduce the weight,increase loading weight,suitable for the production of aerospace equipment,high-speed trains and yachts shell.
5.Friction and sealing materials,friction materials reinforced fiber, significantly improved wear resistance,suitable for high temperature conditions.
STORAGE:
The P-aramid fiber chopped strands should be keep dry in their original bags and stored in a suitable place,preferably at room temperature with 35-65% relative humidity.Avoid the sun, rain and fire.
PACKAGING: