Audited Supplier
8011
0.2--0.27mm
CNC, Drilling, Milling, Cutting, Welding
1%
Available
Factory Inspection List
Fob CIF CFR CNF EXW, etc
According to Order Quantity
ISO9001, ASTM
Mill Finish
Alloy
PP Cap/Ropp Cap
Hot Rolled/Cast Rolled
8000 Series
/H14/H16
Chalco Aluminum
Export Standard Wooden Pallet
According to Customer Requirement
Henan China
7606119000
Product Description
8011 aluminium sheet for PP cap ROPP cap
8011 aluminium lacquered sheet for PP cap ROPP cap
Aludium's Closure Sheets have superb deep-drawing capabilities and lacquer adhesion capabilities. These properties guarantee high quality printing results, giving your closure an impressive finish.A shiny end, in many shapes and colors. Aluminium has exactly the properties that closures need.
Alloy: 8011
Temper: H14
Thickness: 0.17-0.23mm
Width: 800-1000mm
Length: 600mm--1000mm
Surface type:
a. Plain mill finish aluminum strip
b. DOS oil lubricated finish
c. Chromated finish
d. One side golden/white/red/blue/black,etc other colored, other side protective lacquered
e. both sides clear/transparent lacquered
Test item: autoclave test, Hgcl2 test;
Tensile strength: 130-155mpa;
Elongation: 2.5-3.5%;
Earring: 2% Max;
Packing: export standard wooden boxes;
Application :
ROPP cap, PP cap, roll on pilfer proof cap, aluminum pilfer-proof cap, pilfer proof closure, aluminum bottle cap, aluminum screw cap, tear off caps, flip off caps.
8011 aluminium plain strip, aluminium lacquered strip for Injection vial seals
Alloy: 8011
Temper: H14
Thickness: 0.17-0.23mm
Width: 50-900mm
Coil ID: 76mm 152mm
Surface type:
a. Plain mill finish aluminum strip;
b. DOS oil lubricated finish;
c. Chromated finish;
d. One side golden/white/red/blue/black,etc other colored, other side protective lacquered;
e. both sides clear/transparent lacquered;
Test item: autoclave test, Hgcl2 test
Tensile strength: 130-155mpa
Elongation: 2.5-3.5%
Earring: 2% Max
Packing: export standard wooden boxes
Application : vial aluminium seals, aluminium tear off seal, aluminium flip - off vial seals, aluminium closures, pharmaceutical caps, pull-off aluminum cap, aluminum seal cap for injection vial,aluminum cap for injection bottle.
Alloy type 8011 H16 According to EN573-3
1.Chemical Composition : Alloy type 8011 H16 According to EN573-3
2.Size and deviations from the size:
-Thickness tolerance +/- 0.005mm
-Width tolerance -0+0.5mm
-Length tolerance -0+0.5mm
3.Deviations of the forms/shapes:
- Deviations of the straight for hardness of the longitudinal border max 1mm
- Deviation of flatness--max 4mm
- Rectangularity: max difference in the diagonals--3mm
- Dislocation between the sheets--max 2mm
4.Surface of the sheets
The surface of the sheets shall be oil-free, this is controlled by testing with clean natural cotton pads, dipped in 100% distilled water. Laying is steady, without stopping from end to end. Level of oil free, B,C, or D.
Droplets, spots caused by corrosion and burnt lubricant on the surface of the sheets not acceptable.
Minor scratches and staining not acceptable as well.
Surface type:
a.Plain mill finish aluminum strip
b.DOS oil lubricated finish
c.Chromated finish
d.One side golden/white/red/blue/black,etc other colored, other side protective lacquered
e.both sides clear/transparent lacquered
5.Mechnical data:
Resistance to stretching Rm--Min 180 Mpa Max 220 Mpa
Yield strength Rpop Min 145Mpa
Elongation Min 2%
6.Packaging:
Wooden case packing could guarantee the quality of the materials during transportation and storage.
All stacks of the aluminum sheets are bound firmly in nylon, and respectively fixed in wooden cases.
8011 aluminium lacquered sheet for PP cap ROPP cap
Aludium's Closure Sheets have superb deep-drawing capabilities and lacquer adhesion capabilities. These properties guarantee high quality printing results, giving your closure an impressive finish.A shiny end, in many shapes and colors. Aluminium has exactly the properties that closures need.
Alloy: 8011
Temper: H14
Thickness: 0.17-0.23mm
Width: 800-1000mm
Length: 600mm--1000mm
Surface type:
a. Plain mill finish aluminum strip
b. DOS oil lubricated finish
c. Chromated finish
d. One side golden/white/red/blue/black,etc other colored, other side protective lacquered
e. both sides clear/transparent lacquered
Test item: autoclave test, Hgcl2 test;
Tensile strength: 130-155mpa;
Elongation: 2.5-3.5%;
Earring: 2% Max;
Packing: export standard wooden boxes;
Application :
ROPP cap, PP cap, roll on pilfer proof cap, aluminum pilfer-proof cap, pilfer proof closure, aluminum bottle cap, aluminum screw cap, tear off caps, flip off caps.
| Chemical Composition | ||||||||||||
| Alloy | Si | Fe | Cu | Mn | Mg | Cr | Ni | Zn | Ti | Other | Aluminum | |
| Each | Total | |||||||||||
| 8011 | 0.4-0.8 | 0.5-1.0 | 0.1 | 0.1 | 0.1 | 0.1 | - | 0.1 | 0.05 | 0.05 | 0.15 | Remainder |
| Temper | Thickness mm | Tensile Strength Rm MPa | Yield Strength Rp0.2 MPa | Elongation % A50mm | Bend Radius | Hardness HBWa | |||
| H14 | 0.20-0.27 | min. | max. | min. | max. | 180° | 90° | ||
| 120 | 170 | 110 | 1 | 41 | |||||
| H16 | 0.20-0.27 | 160 | 145 | 1 | 50 | ||||
8011 aluminium plain strip, aluminium lacquered strip for Injection vial seals
Alloy: 8011
Temper: H14
Thickness: 0.17-0.23mm
Width: 50-900mm
Coil ID: 76mm 152mm
Surface type:
a. Plain mill finish aluminum strip;
b. DOS oil lubricated finish;
c. Chromated finish;
d. One side golden/white/red/blue/black,etc other colored, other side protective lacquered;
e. both sides clear/transparent lacquered;
Test item: autoclave test, Hgcl2 test
Tensile strength: 130-155mpa
Elongation: 2.5-3.5%
Earring: 2% Max
Packing: export standard wooden boxes
Application : vial aluminium seals, aluminium tear off seal, aluminium flip - off vial seals, aluminium closures, pharmaceutical caps, pull-off aluminum cap, aluminum seal cap for injection vial,aluminum cap for injection bottle.
| Chemical Composition | ||||||||||||
| Alloy | Si | Fe | Cu | Mn | Mg | Cr | Ni | Zn | Ti | Other | Aluminum | |
| Each | Total | |||||||||||
| 8011 | 0.4-0.8 | 0.5-1.0 | 0.1 | 0.1 | 0.1 | 0.1 | - | 0.1 | 0.05 | 0.05 | 0.15 | Remainder |
| Temper | Thickness mm | Tensile Strength Rm MPa | Yield Strength Rp0.2 MPa | Elongation % A50mm | Bend Radius | Hardness HBWa | |||
| H14 | 0.20-0.27 | min. | max. | min. | max. | 180° | 90° | ||
| 120 | 170 | 110 | 1 | 41 | |||||
| H16 | 0.20-0.27 | 160 | 145 | 1 | 50 | ||||
Alloy type 8011 H16 According to EN573-3
1.Chemical Composition : Alloy type 8011 H16 According to EN573-3
2.Size and deviations from the size:
-Thickness tolerance +/- 0.005mm
-Width tolerance -0+0.5mm
-Length tolerance -0+0.5mm
3.Deviations of the forms/shapes:
- Deviations of the straight for hardness of the longitudinal border max 1mm
- Deviation of flatness--max 4mm
- Rectangularity: max difference in the diagonals--3mm
- Dislocation between the sheets--max 2mm
4.Surface of the sheets
The surface of the sheets shall be oil-free, this is controlled by testing with clean natural cotton pads, dipped in 100% distilled water. Laying is steady, without stopping from end to end. Level of oil free, B,C, or D.
Droplets, spots caused by corrosion and burnt lubricant on the surface of the sheets not acceptable.
Minor scratches and staining not acceptable as well.
Surface type:
a.Plain mill finish aluminum strip
b.DOS oil lubricated finish
c.Chromated finish
d.One side golden/white/red/blue/black,etc other colored, other side protective lacquered
e.both sides clear/transparent lacquered
5.Mechnical data:
Resistance to stretching Rm--Min 180 Mpa Max 220 Mpa
Yield strength Rpop Min 145Mpa
Elongation Min 2%
6.Packaging:
Wooden case packing could guarantee the quality of the materials during transportation and storage.
All stacks of the aluminum sheets are bound firmly in nylon, and respectively fixed in wooden cases.
| Chemical Composition | ||||||||||||
| Alloy | Si | Fe | Cu | Mn | Mg | Cr | Ni | Zn | Ti | Other | Aluminum | |
| Each | Total | |||||||||||
| 8011 | 0.4-0.8 | 0.5-1.0 | 0.1 | 0.1 | 0.1 | 0.1 | - | 0.1 | 0.05 | 0.05 | 0.15 | Remainder |
| Temper | Thickness mm | Tensile Strength Rm MPa | Yield Strength Rp0.2 MPa | Elongation % A50mm | Bend Radius | Hardness HBWa | |||
| H14 | 0.20-0.27 | min. | max. | min. | max. | 180° | 90° | ||
| 120 | 170 | 110 | 1 | 41 | |||||
| H16 | 0.20-0.27 | 160 | 145 | 1 | 50 | ||||