Aerospace, Electronics, Medical, Refractory, Structure Ceramic, Industrial Ceramic
95%-99%
Ceramic Parts
White
2100-2500MPa
1700 Degree
3.8GM/Cc
Heat Resistance
280-350 MPa
25-30 W/Mk
RoHS
Alumina Ceramic
INNOVACERA
Carton Packing
Customized
Fujian, China
Product Description
Alumina Ceramic is the most commonly used technical ceramic material. Thanks to its very good electrical insulation, dielectric strength and high temperature resistance up to 1500 °C, Alumina Ceramic is ideal for electrical applications and high-temperature applications.
Alumina ceramics feature:
Good mechanical strength
Good heat conductivity and fire resistance
Good corrosion and wear resistance
Very good electric insulation
The alumina substrates also possess several unique features:
> Good surface with high smoothness/flatness and less porosity
> High resistance to heat shock
> Low warpage and camber
> Stable in very high temperature and corrosive chemical
> Very stable breaking strength and shape/dimension variance
Industrial Ceramic Structure Parts Applications:
Alumina ceramics feature:
Good mechanical strength
Good heat conductivity and fire resistance
Good corrosion and wear resistance
Very good electric insulation
The alumina substrates also possess several unique features:
> Good surface with high smoothness/flatness and less porosity
> High resistance to heat shock
> Low warpage and camber
> Stable in very high temperature and corrosive chemical
> Very stable breaking strength and shape/dimension variance
Industrial Ceramic Structure Parts Applications:
Alumina is the best-known advantaced ceramic material, is widely used in
1.Automotive
2.Petro-chemical
3.Fluid control
4.Material transfer
5.Industry
6.Electrical and electronic
7.Semiconductor
8.Sapphire is single-crystal alumina.
1.Automotive
2.Petro-chemical
3.Fluid control
4.Material transfer
5.Industry
6.Electrical and electronic
7.Semiconductor
8.Sapphire is single-crystal alumina.
Alumina Ceramics Properties | |||
Unit | 95% | 99% | |
Density | g/cm3 | 3.6 | 3.8 |
Water absorption | % | <0.4 | <0.2 |
Firing temperature | °C | 1600 | 1800 |
Hardness | HRA | 70 | 80 |
Coefficientoflinearexpansion | *10-6/°C | 5.5 | 5.3 |
Dielectric constant | 9 | 10.5 | |
Volume resistivity | Ω·cm | - | 1013 |
Breakdownvoltage | KV/mm | 14 | 15 |
Breaking strength | Mpa | 250 | 300 |