D5
Alloy Steel Bar
ASTM
Ferrous Steel Scrap
Hot Rolled, Forged
Round, Square, Flat
Grinded, Peeled, Polished, Rough Turned
Mold Steel
Tool Steel Bar
Uns T30405
Diameter: 20-480mm
ASTM-A681
Annealed, Qunched and Tempered
Grinded, Peeled, Polished, Rough Turned
FUSHUN
Apply The Shipping Packing
Diameter: 20-480mm
Hubei, Huangshi
7228600000
Product Description
Similar Grades:
UNS T30405
Shape:
Round, Flat, Square.
Size Range:
Steel-making Condition:
EF, EF/EAF+LF+VD, EF/EAF+ESR
Delivery Condition:
Annealed , Quenched + Tempered
Surface Condition:
Black, Grinded, Peeled, Rough turned, Polished
Features:
1.Competitive price
2.Immediate delivery
3.Premium quality
4.Reliable service
5.MOQ: 1 Ton
Chemical Composition(%)
Physical Properties
The physical properties of D5 tool steels are outlined in the following table:
Mechanical Properties
The mechanical properties of D5 tool steels are tabulated below.
Fabrication and Heat Treatment
Heat Treatment
D5 steels should be preheated very slowly up to 815°C (1500°F), then temperature should be increased to 1009°C (1850°F) and held for 20 to 45 minutes. Then they are air quenched.
Forging
Forging of D5 steels can be done at 1065°C (1950°F) down to 1750°F. Do not forge below 926°C (1700°F).
Annealing
Annealing of D5 steels should be done at 886°C (1627°F) followed by slow furnace cooling at 4°C (40°F) per hour or less.
Tempering
D5 steels can be tempered at 204°C (400°F) for achieving Rockwell C hardness of 61 and at 537°C (1000°F) for a Rockwell C hardness of 54.
Applications
Applications of D5 steels include thread rolling, blanking or forming dies operating at temperatures below 482°C (900°F).
UNS T30405
Shape:
Round, Flat, Square.
Size Range:
| Diameter(mm) | Thickness (mm) | Width (mm) | Length(mm) | |
| Round | 20-480 | - | - | 2000-5800 |
| Square | 20-480 | - | - | 2000-5800 |
| flat | - | 20-50 | 80-600 | 2000-5800 |
Steel-making Condition:
EF, EF/EAF+LF+VD, EF/EAF+ESR
Delivery Condition:
Annealed , Quenched + Tempered
Surface Condition:
Black, Grinded, Peeled, Rough turned, Polished
Features:
1.Competitive price
2.Immediate delivery
3.Premium quality
4.Reliable service
5.MOQ: 1 Ton
| Packing details | In seaworthy packing, as your requirement. |
| Delivery details | within 30-50 days |
| C | Mn | P | S | Si | Cr | W | V | Mo | Co |
| 1.4-1.60 | 0.10-0.60 | <= 0.030 | <=0.030 | 0.10-0.60 | 11.00-13.00 | / | 1.00max | 0.70-1.20 | 2.50-3.50 |
Physical Properties
The physical properties of D5 tool steels are outlined in the following table:
| Properties | Metric | Imperial |
| Density | 7.7 - 8.03 x 1000 kg/m3 | 0.278 - 0.290 lb/in3 |
| Melting point | 1426°C | 2600°F |
Mechanical Properties
The mechanical properties of D5 tool steels are tabulated below.
| Properties | Metric | Imperial |
| Poisson's ratio | 0.27-0.30 | 0.27-0.30 |
| Elastic modulus | 190-210 GPa | 27557-30457 ksi |
Fabrication and Heat Treatment
Heat Treatment
D5 steels should be preheated very slowly up to 815°C (1500°F), then temperature should be increased to 1009°C (1850°F) and held for 20 to 45 minutes. Then they are air quenched.
Forging
Forging of D5 steels can be done at 1065°C (1950°F) down to 1750°F. Do not forge below 926°C (1700°F).
Annealing
Annealing of D5 steels should be done at 886°C (1627°F) followed by slow furnace cooling at 4°C (40°F) per hour or less.
Tempering
D5 steels can be tempered at 204°C (400°F) for achieving Rockwell C hardness of 61 and at 537°C (1000°F) for a Rockwell C hardness of 54.
Applications
Applications of D5 steels include thread rolling, blanking or forming dies operating at temperatures below 482°C (900°F).