Product Description
Production Description
1- Product Induction
KH-1166 is a silicon-modified styrene-acrylic polymer emulsion developed with APEO-free environment-friendly high-quality additives and special monomers. Reasonable monomer ratio and strict process control, Gives this emulsion an exceptionally balanced performance.
2-Features
High pigment and filler loading capacity, low dosage, good scrub resistance.
APEO Environmentally friendly, non-toxic and APEO-free.
Good adhesion and water resistance
The coating film has good gloss, high hardness, and high gloss retention after dilution.
The color is fully displayed and durable, and it does not affect the color display after dilution.
3-Application
This product is widely used in various environmental-friendly interior and exterior wall latex paints, handicraft paints, water-based industrial paints, water-based inks and high-gloss finish paints.
4-Technical Parameter
| Appearance | Milky white bluish liquid |
Solid Content % | 44~46% |
PH | 7.0~9.0 |
Viscosity(NDJ-1,No.3,60rpm,25ºC,mPa·s) | 200~800cps |
Minimum film forming temperature (MFT) (ºC) | 28ºC |
5-Package &Storage
25KG 50KG 200KG plastic drum and IBC tank.
About Us
Shandong Kunhan New Material Technology Co., Ltd. was established in 2006 and is located in Linzi District, Zibo City, the ancient capital of Qi State. The company has a registered capital of 10 million yuan and covers an area of 20,000 square meters. It is a comprehensive modern high-tech enterprise integrating R&D, production and sales of water-based acrylic emulsions, water-based nano-coatings and new fluorine-containing materials. There is a set of acrylic emulsion production equipment with an annual production capacity of 50,000 tons, a set of multifunctional monomer equipment with an annual production capacity of 600 tons, and a R&D center. The company has 113 employees, including 32 R&D personnel, and more than 60% of the employees have a college degree or above.