Product Description
Product Name:ALUMINUM CONDUCTOR COMPOSITE CORE
1,Definition: Is a high capacity, low slag conductor which consists of a carbon fiber composite core encased in a protective fiberglass sheath that is helically wrapped with high purity conductive aluminum strands.
2,Application:It is a new type of overhead transmission line conductor, its outstanding characteristics are light weight, tensile resistance, good thermal stability, small relaxation, strong flow capacity per unit area and corrosion resistance. Especially suitable for the company's resident coastal, mining areas with high corrosion intensity, pollution intensity, easy to run wire operating environment.
3,Standard:GB/T 32502-2016; Q/320282 DFP08-2017; Q/320282 DFP05-2017;
4, Packing:Wooden steel wood drum or Steel drum
5,Technical Parameter:
| ACCC | Cond. | Dia. | Core Dia. | Weight | Core Related Strength | Cond. Rated Strength | ACCC | Cond. | Dia. |
| International Sizes | (kcmil) | (mm2) | (mm) | (mm) | (kg/km) | (kN) | (ohm/km) | 180°C | 200°C |
| Copenhagen | 434 | 219.9 | 18.29 | 5.97 | 661 | 60.4 | 0.2094 | 1,017 | 1,070 |
| Lisbon | 623 | 315.5 | 21.79 | 7.11 | 948 | 85.7 | 0.1460 | 1,284 | 1,353 |
| Brussels | 832 | 421.4 | 25.15 | 8.13 | 1265 | 112.0 | 0.1097 | 1,549 | 1,632 |
| Hamburg | 1078 | 546.4 | 28.63 | 8.76 | 1627 | 130.2 | 0.0846 | 1,834 | 1,935 |
| Milan | 1120 | 567.7 | 29.11 | 8.76 | 1686 | 130.2 | 0.0813 | 1,880 | 1,984 |
| Rome | 1169 | 592.5 | 29.90 | 9.53 | 1774 | 153.8 | 0.0780 | 1,935 | 2,043 |
| Vienna | 1242 | 629.2 | 30.43 | 8.76 | 1853 | 130.2 | 0.0733 | 2,007 | 2,119 |
| Munich | 1447 | 733.1 | 32.84 | 9.53 | 2170 | 153.8 | 0.0632 | 2,211 | 2,336 |
| London | 1498 | 759.0 | 33.40 | 9.78 | 2248 | 162.1 | 0.0609 | 2,264 | 2,392 |
| Paris | 1606 | 813.7 | 34.16 | 8.76 | 2366 | 130.2 | 0.0568 | 2,358 | 2,492 |
| Berlin (Madrid-lce) | 1986 | 1006.5 | 38.20 | 10.54 | 2949 | 188.3 | 0.0458 | 2,713 | 2,872 |
| Madrid | 1999 | 1013.0 | 38.20 | 9.78 | 2948 | 162.1 | 0.0454 | 2,721 | 2,880 |
| Athens | 2782 | 1409.6 | 44.75 | 10.54 | 4066 | 188.3 | 0.0328 | 3,335 | 3,538 |
6,Product Type:
| Type | Shape | Dia. of core mm | Area of Al mm2 | Rate break loading KN | Unit weight Kg/km | 20°C DC Ω/km | Line expansion Factor X10-6 1/ºC | |
| Under turning point | Above turning point | |||||||
| The formed annealed aluminum conductors composite core supported | ||||||||
| 95/30~800/95 | 6.00~11.00 | 95~800 | 64.85~245.7 | 318.5~2406.5 | 0.2939~0.0351 | 15.1~18.9 | 1.8 | |
| Thermal-resistant Aluminum-alloy Conductors Composite Core Reinforced | ||||||||
| 150/35~630/70 | 6.50~9.50 | 182.0~710.8 | 76.97~213.4 | 477.40~1907.45 | 0.1972~0.0459 | 16.5~19.2 | 1.8 | |
| Formed Intermediate Aluminum Conductors Composite Core Supported | ||||||||
| 95/30~1660/95 | 6.00~11.00 | 95~1660 | 69.30~373.0 | 317.19~4811.7 | 0.0173~0.2971 | 15.2~20.8 | 1.8 | |
| 150/35~630/70 | 6.50~9.50 | 182.00~710.80 | 83.94~228.27 | 477.40~1907.45 | 0.0459~0.1972 | 16.5~19.2 | 1.8 | |
| The High-elongation Hard Aluminum ConductorsComposite Core Reinforced | ||||||||
| 150/30~630/70 | 6.00~9.50 | 154.2~639.9 | 73.7~221.5 | 482.0~1910.2 | ≤0.1871 | 17.3~19.2 | 1.8 | |
| The High-conductivity (62.5% IACS) Aluminum ConductorsComposite Core Reinforced | ||||||||
| 150/30~630/70 | 6.00~9.50 | 154.2~639.9 | 72.1~213.6 | 479.1~1903.8 | ≤0.1841 | 17.3~19.2 | 1.8 | |