Mflam 1400
Aluminum Hypophosphite Flame Retardant for Polyester Based TPU
Specification:
Application:
Mflam 1400 is a halogen-free flame retardant for polyester based TPU. It mainly acts as a flame retardant by the condensed phase flame retardant mechanism. It has the advantages of low added amount and high flame retardant efficiency. The surface of treated TPU is smooth, with strong resistance to precipitation, good water resistance, excellent migration resistance, superior electrical properties and low smoke and non-toxicity.
Shipping Information:
The package is 25kg craft paper bag or on customer's request, and can be loaded 17.5mt with pallet in 1x 20'FCL.
Remarks:
(1) The initial thermal decomposition temperature of Mflam 1400 in air is about 320 °C, so the processing temperature of the twin-screw can be adjusted according to the specific conditions to enhance the dispersion and enhance the plasticization effect. A certain degree of hollowness must be maintained during the twin-screw extrusion process.
(2) When applying Mflam 1400, please pay attention to the use of stabilizers, coupling agents, and other phosphorus and nitrogen flame retardants APP, MC or MCA, together with 1400.
Application Examples
1. Formulation and performance:
Remarks:all the data above is the classical application test data of Mflam 1400.
2. Process:
Machine: twin screw 35
Main engine termperature (ºC): 160 170 170 180 180 180 180 180 170 160
Main engine speed: 240-360rpm
Recommended screw: 35 (46 thread blocks, length 1428mm)
Feel free to contact us!
Aluminum Hypophosphite Flame Retardant for Polyester Based TPU
Specification:
| Item | Index | |
| Appearance | White Powder | |
| The Content of Phosphorus %(W/W) | ≥32 | |
| The Content of Nitrogen %(W/W) | ≥11 | |
| Particle Size D50, μm D90, μm | 6±5 25±4 | |
| Moisture %(W/W) | ≤0.5 | |
| TGA (20ºC/min, in N2, ) | Weight Loss 1% | ≥300ºC |
| Weight Loss 5% | ≥310ºC | |
Application:
Mflam 1400 is a halogen-free flame retardant for polyester based TPU. It mainly acts as a flame retardant by the condensed phase flame retardant mechanism. It has the advantages of low added amount and high flame retardant efficiency. The surface of treated TPU is smooth, with strong resistance to precipitation, good water resistance, excellent migration resistance, superior electrical properties and low smoke and non-toxicity.
Shipping Information:
The package is 25kg craft paper bag or on customer's request, and can be loaded 17.5mt with pallet in 1x 20'FCL.
Remarks:
(1) The initial thermal decomposition temperature of Mflam 1400 in air is about 320 °C, so the processing temperature of the twin-screw can be adjusted according to the specific conditions to enhance the dispersion and enhance the plasticization effect. A certain degree of hollowness must be maintained during the twin-screw extrusion process.
(2) When applying Mflam 1400, please pay attention to the use of stabilizers, coupling agents, and other phosphorus and nitrogen flame retardants APP, MC or MCA, together with 1400.
Application Examples
1. Formulation and performance:
| UL94 | Tensile Strength (MPa) | Elongation at break (%) | Hardness | |
| TPU-785A+12% Mflam 1400+1% additive | V-0(3.2mm) V-1(1.6mm) | 9 | 434.3 | 87 |
| TPU-785A+16% Mflam 1400+1% additive | V-0(3.2mm) V-0(1.6mm) | 8.9 | 432.7 | 88 |
2. Process:
Machine: twin screw 35
Main engine termperature (ºC): 160 170 170 180 180 180 180 180 170 160
Main engine speed: 240-360rpm
Recommended screw: 35 (46 thread blocks, length 1428mm)