1. Brief introduction
Aluminum rod continuous casting and rolling line can produce three kinds of conductive aluminum rods of 15mm, 12mm, 9.5mm.
15mm aluminum rod is produced by 10 rolling stands;
12mm aluminum rod is produced by 12 rolling stands;
9.5mm aluminum rod is produced by 14 rolling stands.
2. Process Flow
2.1 Aluminum ingot and scrap aluminum wire-alumInum melting furnace --four-wheel horizontal continuous casting machine- oil-pressure shearer -continuous rolling mill - coiler with dual basket - aluminum rod
2.2. Melt aluminum or melt aluminum molten which is stored in the holding furnace will be injected to four-wheel continuous casting machine through launders. The sectional area of trapezoidal casting ingot is2, 330mm² , Scrap aluminum bar is cut by oil-pressure shearer and then acceptable aluminum bars are sent to continuous rolling mill, after emulsion bag, guiding wheel, leading pipe and take-up coiler, the rod will become looping.
3. Main Technical Parameters
4. Supply of scope
4.1. Four-wheel Continuous Casting Machine (with 2PCS of casting ladles)
4.2. Single-Track Oil Hydraulic Shearer
4.3. Continuous Rolling Mill
4.4. Emulsion Lubrication System for Rolling Mill
4.5. Lubrication System for Gearbox
4.6. Emulsion bag, Guiding wheel and Leading Pipe
4.7. Coiler and Coiler with Dual Basket Trolley
4.8. Electrical Control Device
Aluminum rod continuous casting and rolling line can produce three kinds of conductive aluminum rods of 15mm, 12mm, 9.5mm.
15mm aluminum rod is produced by 10 rolling stands;
12mm aluminum rod is produced by 12 rolling stands;
9.5mm aluminum rod is produced by 14 rolling stands.
2. Process Flow
2.1 Aluminum ingot and scrap aluminum wire-alumInum melting furnace --four-wheel horizontal continuous casting machine- oil-pressure shearer -continuous rolling mill - coiler with dual basket - aluminum rod
2.2. Melt aluminum or melt aluminum molten which is stored in the holding furnace will be injected to four-wheel continuous casting machine through launders. The sectional area of trapezoidal casting ingot is2, 330mm² , Scrap aluminum bar is cut by oil-pressure shearer and then acceptable aluminum bars are sent to continuous rolling mill, after emulsion bag, guiding wheel, leading pipe and take-up coiler, the rod will become looping.
3. Main Technical Parameters
| NO. | Technical parameter | Date |
| 1 | Diameter (finished EC-aluminum) | 9.5, 12, 15mm |
| 2 | Max. Capacity | 6t/h |
| 3 | Coil's weight | ~2t |
| 4 | Overall weight of main equipment | ~ 65t |
| 5 | Overall power of main equipment | ~470kW (excluding furnace) |
| 6 | Finished rolling speed | ≤ 8.17m/s |
| 7 | Overall dimension: Approx. | 32.1× 7.2× 4.2m (L × W × H) |
4. Supply of scope
4.1. Four-wheel Continuous Casting Machine (with 2PCS of casting ladles)
4.2. Single-Track Oil Hydraulic Shearer
4.3. Continuous Rolling Mill
4.4. Emulsion Lubrication System for Rolling Mill
4.5. Lubrication System for Gearbox
4.6. Emulsion bag, Guiding wheel and Leading Pipe
4.7. Coiler and Coiler with Dual Basket Trolley
4.8. Electrical Control Device