JHSW-8608 B1 Fire-retardant High Oxygen Index Fire-Resistent Polyurea has excellent fire resistant property, and at the same time remain good physical property. It can be used for waterproofing application where good fire resistant property is required.Advantages:
- Fast cure, short down time, no sagging
- Excellent physical properties
- Excellent fire resistant property.
- Bondable and paintable to various kinds of substrates
- 0 VOC, Non-Toxic
- Anti-corrosion and Waterproof Properties
- Seamless, flexible, slick and non-porous
JHSW-8608 B1 Fire-retardant High Oxygen Index Fire-Resistent Polyurea can be applied at thicknesses of several ten millimeters, or greater, in a single application. It can be used for waterproofing application where good flame-resistant property is required.
Properties:
| Tensile Strength /MPa | ≥16 | Solids Content/% | 100 |
| Elongation/% | ≥250 | VOC | 0 |
| Tear Strength/( N/mm) | ≥85 | Gel Time/s | 8-10 |
| Shore Hardness | ≥88A | Tack Free/ s | 12-15 |
| Adhesion /(Pull off, steel,MPa) | ≥10 | Shelf Life | 12 months, unopened at 0~40 ºC |
| Density/( g/cm3) | 0.95~1.05 | Flash Point/ ºC | >100 |
| Abrasion Resistance /(GB/T 1689-1998, cm3/1.61km, g) | ≤0.04 | Mix Ratio V/V | 1: 1 |
| Impermeability(0.3MPa/30min) | Impervious | Recommended Spreading Thickness/mm | 2~3 |
| Oxygen index | 30.2 | Colors: | Optional |