Product Description
Metallizable base film: The product has good thickness uniformity, stable electrical properties, good winding property, good metal evaporation ability, and the main thickness specification of the product is 2.4micro to 12 micro.
Product application scope: metallized base film and metallized coating are mainly used in: new energy industry: photovoltaic inverter, wind power converter, etc.; power industry: large high frequency switching power supply, UPS, emergency power EPS, intermediate frequency power supply, DC stabilized power supply, electroplating power supply, chemical power supply, etc.; electric locomotive industry: locomotive traction converter, Metro, high-speed rail, light rail, etc , tram; power quality industry: dynamic synchronous var compensator SVG, active power filter APF, etc.; energy saving industry: high voltage inverter, etc.; home appliance industry: filter protection, etc.
BOPP metalized base film for capacitor
BOPP hazy film for capacitor
Product application scope: metallized base film and metallized coating are mainly used in: new energy industry: photovoltaic inverter, wind power converter, etc.; power industry: large high frequency switching power supply, UPS, emergency power EPS, intermediate frequency power supply, DC stabilized power supply, electroplating power supply, chemical power supply, etc.; electric locomotive industry: locomotive traction converter, Metro, high-speed rail, light rail, etc , tram; power quality industry: dynamic synchronous var compensator SVG, active power filter APF, etc.; energy saving industry: high voltage inverter, etc.; home appliance industry: filter protection, etc.
BOPP metalized base film for capacitor
Items | Test Methods | Units | Typical Value | |
| Thickness | GB 6672 | μm | 7 | |
| Ave. Variation of Thickness | GB/T13541 | % | +0.2 | |
| Tensile strength (MD/TD) | GB 13022 | MPa | 160/280 | |
| Elongation at Break (MD/TD) | GB 13022 | % | 145/50 | |
| Heat Shrinkage (MD/TD) | MP-1 | GB 12026 | % | 3.5/0.5 |
| MP-H | 3.0/0.1 | |||
| Density | GB 1033 | g/cm3 | 0.91 | |
| Surface Roughness(in/out) | GB/T13541 | μm | 0.08/0.08 | |
| Wet Tension (Treated Side) | GB/T 14216 | mN/m | 40 | |
| Dielectric Strength(Ave/Min)DC | GB/T13541 | V/μm | 496/406 | |
| Dielectric Constant | GB/T 13541 | -- | 2.2 | |
| Dielectric Consumed Angle tangent | GB/T 13541 | -- | 2.0×10-4 | |
| Volume Resistivity | GB/T 13541 | Ω·m | 1.9×1015 | |
BOPP hazy film for capacitor
Items | Units | Typical Value | ||
| Thickness | μm | 15 | ||
| Ave. Variation of Thickness | % | +0.2 | ||
| Tensile strength (MD/TD) | MPa | 155/258 | ||
| Elongation at Break (MD/TD) | % | 125/49 | ||
| Heat Shrinkage (MD/TD) | % | 3.0/0.3 | ||
| Voidage | Average | % | 10.6 | |
| Max. | 11.1 | |||
| Min | 10.1 | |||
| Dielectric Strength DC | Average | V/μm | 550 | |
| Min. | 515 | |||
| Electric strength (d.c. test) | Central value | V/μm | 356 | |
| Not more than 1 of 21 results shall be below | 305 | |||
| Dielectric Constant | -- | 2.2 | ||
| Dissipation factor | -- | 2.0×10-4 | ||
| Volume Resistivity | Ω·m | 3.2×1015 | ||
| Surface Roughness(In/Out) | Ra | μm | 0.42/0.40 | |
Items | Units | Typical Value | ||
| Thickness | μm | 15 | ||
| Ave. Variation of Thickness | % | +0.2 | ||
| Tensile strength (MD/TD) | MPa | 155/258 | ||
| Elongation at Break (MD/TD) | % | 125/49 | ||
| Heat Shrinkage (MD/TD) | % | 3.0/0.3 | ||
| Voidage | Average | % | 10.6 | |
| Max. | 11.1 | |||
| Min | 10.1 | |||
| Dielectric Strength DC | Average | V/μm | 550 | |
| Min. | 515 | |||
| Electric strength (d.c. test) | Central value | V/μm | 356 | |
| Not more than 1 of 21 results shall be below | 305 | |||
| Dielectric Constant | -- | 2.2 | ||
| Dissipation factor | -- | 2.0×10-4 | ||
| Volume Resistivity | Ω·m | 3.2×1015 | ||
| Surface Roughness(In/Out) | Ra | μm | 0.42/0.40 | |