MadeInChina.com > Chemicals > Plastic Products > Plastic Film

BOPP Film 3mic-20mic for Capacitor Application AC/DC Capacitors

Price	$4.30 Compare
Min Order	1000 kg
Availability	In Stock
Shipping From	Guangdong, China
Popularity	325 people viewed
Quantity	+-

FSPG HI-TECH CO., LTD.

Audited Supplier 6 years

Profile Certified by SGS/BV

Guangdong, China
Waven (Ms.)
Sales Manager

Visit Homepage Product Catalog

Product Detail
Contact Supplier

Type:

Film

Transparency:

Transparent

Hardness:

Soft

for Metallization:

MP-1

High Temperature Resistance:

MP-H

Trademark:

FSPG Products

Origin:

Foshan, Guangdong, China

HS Code:

3920209090

Product Description

BOPP metalized base film for capacitor

Items		Test Methods	Units	Typical Value
Thickness		GB 6672	μm	7
Ave. Variation of Thickness		GB/T13541	%	+0.2
Tensile strength (MD/TD)		GB 13022	MPa	160/280
Elongation at Break (MD/TD)		GB 13022	%	145/50
Heat Shrinkage (MD/TD)	MP-1	GB 12026	%	3.5/0.5
Heat Shrinkage (MD/TD)	MP-H	GB 12026	%	3.0/0.1
Density		GB 1033	g/cm³	0.91
Surface Roughness(in/out)		GB/T13541	μm	0.08/0.08
Wet Tension (Treated Side)		GB/T 14216	mN/m	40
Dielectric Strength(Ave/Min)DC		GB/T13541	V/μm	496/406
Dielectric Constant		GB/T 13541	--	2.2
Dielectric Consumed Angle tangent		GB/T 13541	--	2.0×10^-4
Volume Resistivity		GB/T 13541	Ω·m	1.9×10¹⁵

BOPP hazy film for capacitor

Items			Units	Typical Value
Thickness			μm	15
Ave. Variation of Thickness			%	+0.2
Tensile strength (MD/TD)			MPa	155/258
Elongation at Break (MD/TD)			%	125/49
Heat Shrinkage (MD/TD)			%	3.0/0.3
Voidage	Average		%	10.6
	Max.			11.1
	Min			10.1
Dielectric Strength DC	Average		V/μm	550
	Min.			515
Electric strength (d.c. test)	Central value		V/μm	356
	Not more than 1 of 21 results shall be below			305
Dielectric Constant			--	2.2
Dissipation factor			--	2.0×10^-4
Volume Resistivity			Ω·m	3.2×10¹⁵
Surface Roughness(In/Out)		Ra	μm	0.42/0.40

Items			Units	Typical Value
Thickness			μm	15
Ave. Variation of Thickness			%	+0.2
Tensile strength (MD/TD)			MPa	155/258
Elongation at Break (MD/TD)			%	125/49
Heat Shrinkage (MD/TD)			%	3.0/0.3
Voidage	Average		%	10.6
	Max.			11.1
	Min			10.1
Dielectric Strength DC	Average		V/μm	550
	Min.			515
Electric strength (d.c. test)	Central value		V/μm	356
	Not more than 1 of 21 results shall be below			305
Dielectric Constant			--	2.2
Dissipation factor			--	2.0×10^-4
Volume Resistivity			Ω·m	3.2×10¹⁵
Surface Roughness(In/Out)		Ra	μm	0.42/0.40