MadeInChina.com > Chemicals > Plastic Products > Plastic Film

BOPP Film for Metallized and Capacitor

Price	$4.30 Compare
Min Order	1000 kg
Availability	In Stock
Shipping From	Guangdong, China
Popularity	389 people viewed
Quantity	+-

FSPG HI-TECH CO., LTD.

Audited Supplier 6 years

Profile Certified by SGS/BV

Guangdong, China
Waven (Ms.)
Sales Manager

Visit Homepage Product Catalog

Product Detail
Contact Supplier

Material:

BOPP

Type:

Stretch Film

Transparency:

Opaque

Hardness:

Soft

Molding method:

Multiple Extrusion

for Metallization:

MP-1

High Temperature Resistance:

MP-H

Trademark:

FSPG Products

Transport Package:

Pallet

Specification:

Pallet

Origin:

Foshan, Guangdong, China

HS Code:

3920209090

Product Description

MP-1 is a film for metallization which to be used as dielectric metarials for Capacitors.

MP-H is a film for metallization which to be used as dielectric meterials for Capacitors with high temperature resistance.
BOPP metalized based film for capacitor

Items		Test Methods	Units	Typical Value
Thickness		GB 6672	μm	7
Ave. Variation of Thickness		GB/T13541	%	+0.2
Tensile strength (MD/TD)		GB 13022	MPa	160/280
Elongation at Break (MD/TD)		GB 13022	%	145/50
Heat Shrinkage (MD/TD)	MP-1	GB 12026	%	3.5/0.5
Heat Shrinkage (MD/TD)	MP-H	GB 12026	%	3.0/0.1
Density		GB 1033	g/cm³	0.91
Surface Roughness(in/out)		GB/T13541	μm	0.08/0.08
Wet Tension (Treated Side)		GB/T 14216	mN/m	40
Dielectric Strength(Ave/Min)DC		GB/T13541	V/μm	496/406
Dielectric Constant		GB/T 13541	--	2.2
Dielectric Consumed Angle tangent		GB/T 13541	--	2.0×10^-4
Volume Resistivity		GB/T 13541	Ω·m	1.9×10¹⁵

BOPP hazy film for capacitor

Items			Units	Typical Value
Thickness			μm	15
Ave. Variation of Thickness			%	+0.2
Tensile strength (MD/TD)			MPa	155/258
Elongation at Break (MD/TD)			%	125/49
Heat Shrinkage (MD/TD)			%	3.0/0.3
Voidage	Average		%	10.6
	Max.			11.1
	Min			10.1
Dielectric Strength DC	Average		V/μm	550
	Min.			515
Electric strength (d.c. test)	Central value		V/μm	356
	Not more than 1 of 21 results shall be below			305
Dielectric Constant			--	2.2
Dissipation factor			--	2.0×10^-4
Volume Resistivity			Ω·m	3.2×10¹⁵
Surface Roughness(In/Out)		Ra	μm	0.42/0.40