Product Description
Bare Single-Mode G652D/G657/G654 Bend-Optimized Low Loss Optical FiberBending Insensitive Single-mode Fibre
• Short pitch cables for special application
• High performance optical network operating in O-E-S-C-L band
• High speed optical routes in buildings (FTTx)
• Cables with low bending requirements
Product standards
Applications
| Specifications (G657A1) | ||||
| Characteristics | Conditions | Specified values | Units | |
| Optical Characteristics | ||||
| Attenuation | 1310nm | ≤0.35 | [dB/km] | |
| 1383nm(after H2-aging) | ≤0.35 | [dB/km] | ||
| 1460nm | ≤0.25 | [dB/km] | ||
| 1550nm | ≤0.21 | [dB/km] | ||
| 1625nm | ≤0.23 | [dB/km] | ||
| Attenuation vs. Wavelength | 1285-1330nm, in reference to 1310nm | ≤0.03 | [dB/km] | |
| Max. α difference | 1525-1575nm, in reference to 1550nm | ≤0.02 | [dB/km] | |
| 1285-1340nm | -3.5 to 3.5 | [ps/(nm·km)] | ||
| Dispersion Coefficient | 1550nm | ≤18 | [ps/(nm·km)] | |
| 1625nm | ≤22 | [ps/(nm·km)] | ||
| Zero Dispersion Wavelength(λ0) | -- | 1300-1324 | [nm] | |
| Zero Dispersion Slope(S0) | -- | ≤0.092 | [ps/(nm2·km)] | |
| Typical Value | -- | 0.086 | [ps/(nm2·km)] | |
| PMD | Maximum Individual Fibre | -- | ≤0.1 | [ps/√km] |
| Link Design Value(M=20,Q=0.01%) | -- | ≤0.06 | [ps/√km] | |
| Typical Value | -- | 0.04 | [ps/√km] | |
| Cable Cutoff Wavelength (λCC) | -- | ≤1260 | [nm] | |
| Mode Field Diameter(MFD) | 1310nm | 8.4-9.2 | [μm] | |
| 1550nm | 9.3-10.3 | [μm] | ||
| Effective Group Index of Refraction(Neff ) | 1310nm | 1.466 | -- | |
| 1550nm | 1.467 | -- | ||
| Point Discontinuities | 1310nm | ≤0.05 | [dB] | |
| 1550nm | ≤0.05 | [dB] | ||
| Geometrical Characteristics | ||||
| Cladding Diameter | -- | 125.0±0.7 | [μm] | |
| Cladding Non-Circularity | -- | ≤0.7 | [%] | |
| Coating Diameter | -- | 235-245 | [μm] | |
| Coating-Cladding Concentricity Error | -- | ≤12.0 | [μm] | |
| Coating Non-Circularity | -- | ≤6.0 | [%] | |
| Core-Cladding Concentricity Error | -- | ≤0.5 | [μm] | |
| Curl(radius) | -- | ≥4 | [m] | |
| Delivery Length | -- | Up to 50.4 | [km/reel] | |
| Environmental Characteristics | 1310nm, 1550nm & 1625nm | |||
| Temperature Dependence Induced Attenuation | -60ºC to +85ºC | ≤0.05 | [dB/km] | |
| Temperature-Humidity Cycling Induced Attenuation | -10°C to +85°C, 98% RH | ≤0.05 | [dB/km] | |
| Watersoak Dependence Induced Attenuation | 23°C, for 30 days | ≤0.05 | [dB/km] | |
| Damp Heat Dependence Induced Attenuation | 85°C and 85% RH, for 30 days | ≤0.05 | [dB/km] | |
| Dry Heat Aging | 85ºC, for 30 days | ≤0.05 | [dB/km] | |
| Mechanical Specification | ||||
| Proof Test | -- | ≥9.0 | [N] | |
| -- | ≥1.0 | [%] | ||
| -- | ≥100 | [kpsi] | ||
| Macro-bend Induced Loss | 10 Turns Around a Mandrel of 15 mm Radius | 1550nm | ≤0.25 | [dB] |
| 10 Turns Around a Mandrel of 15 mm Radius | 1625nm | ≤1.0 | [dB] | |
| 1 Turn Around a Mandrel of 10 mm Radius | 1550nm | ≤0.75 | [dB] | |
| 1 Turn Around a Mandrel of 10 mm Radius | 1625nm | ≤1.5 | [dB] | |
| Coating Strip Force | typical average force | 1.5 | [N] | |
| peak force | 1.3-8.9 | [N] | ||
| Dynamic Fatigue Parameter (nd) | -- | ≥20 | -- | |