Audited Supplier
Products Features:
1,100% biodegradable.
2,Compared to the traditional plastic, save over 75% petrochemical resource.
3,Compared to the traditional plastic ,it can reduce over 60% co2 emission.
4,No phthalate, no bisphenol A, non-toxic and pollution-free.
5,Have mechanical prooerties,can applied to general plastic processing facilities for various modding processing.
6,Transparency and softness could be regulate as required
Product Details:
Properties: biodegradable, environmental friendly, the film bag is transparent, and with good loading capicity.
Size: Thickness 15 micron to 50 micron., different size can be done to meet customers.
Width: 200mm to 1600mm
Length: 4000m
Type: 100% biodegradable bags
Application :Household Care, Daily use
Feature Eco-Friendly
Place of Origin: zhenJiang, China (Mainland)
Brand Name: TORISE
Model Number: TRBM01Material: PBAT, Cornstarch,PLA
Compostability: 100%compostable
Biodegradability: 100%biodegradable
Color Optional
OEM Avaliable
Certification EN13432/OK COMPOST
Materials technical data
TRBM01 MATERIALS:
Items | standard | Unit | TRBM01 |
Density | ISO1183 | g/cm3 | 1.18-1.2 |
Melting Point | DSC, 10°C/min | °C | 110-120 |
Melt Flow index | ISO1133 | g/10min (190 °C,2.16kg) | ≤10 |
Tensile Strength | ISO527 | MPa | ≥12 |
Elongation at Break | ISO527 | % | ≥180 |
Bending Strength | ISO178 | MPa | ≥4 |
Flexural Modulus | ISO178 | MPa | ≥100 |
TRBM02 MATERIALS:
Items | standard | Unit | TRBM02 |
Density | ISO1183 | g/cm3 | 1.2-1.3 |
Melting Point | DSC, 10°C/min | °C | 155-170 |
Melt Flow index | ISO1133 | g/10min (190 °C,2.16kg) | ≤15 |
Tensile Strength | ISO527 | MPa | ≥20 |
Elongation at Break | ISO527 | % | ≥150 |
Bending Strength | ISO178 | MPa | ≥15 |
Flexural Modulus | ISO178 | MPa | ≥500 |