| Material | 100% New Virgin Raw Material |
| Thickness | 1.8(CAST ACRYLIC SHEET MINIMUM THICKNESS), 2, 3, 4, 5, 8,10,15,20, 30, 50,60mm (1.8-60mm) |
| Color | transparent(clear), white, opal, black, red, green, blue, yellow, etc. OEM color OK |
| Standard size | 1220x1830, 1220x2440,2050x3050,1220x3050 mm,1350x2000,1500x3000, 1250x1850,1250x2450,1050x2050mm |
| Certificate | CE,DE, REACH,ROHS and ISO 9001 |
| Equipment | Imported glass models (from Pilkington Glass in U. K. ) |
| MOQ | 36 pieces,can be mixed with colors/sizes/thickness |
| Delivery | 10-25 days |
| Super Transparent | looks like crystal,light transmittance up to 93% |
General Cast Acrylic Sheet characters:
1) High transmittance up to 93%;
2) Light weight: less than half as heavy as glass;
3) Excellent weather resistance to against discoloration and deformation;
4) Exceptional impact resistance: 7-16 times greater impact resistance than glass;
5) Excellent chemical and mechanical resistance: resistance to acid and alkali;
6) Ease of Fabrication: Acrylic sheet can be s painted, silk-screened, vacuum-coated, and also can be sawed, drilled, and machined
to form almost any shape when heated to a pliable state.
Top-grade JUMEI cast acrylic sheets made from only 100% virgin raw material.
All JUMEI acrylic sheets are UV coated, guarantee sheets not yellow when using outside, can use outdoor for 8-10 years.
No smell when cut them by laser or CNC machine, easily bendable and formable.
Protective paper are imported from Malaysia, thicker durable and easy to laminate,easily to remove, no glue left.
Best thickness tolerance and sufficient thickness.
| Physical Property of Cast Acrylic sheet | |||
PROPERTY | UNIT | VALUE | |
MECHANICAL | Specific Gravity | - | 1.19-1.2 |
Roswell Hardness | kg/cm 2 | M-100 | |
Shear Strength | kg/cm 2 | 630 | |
Flexural Strength | kg/cm 2 | 1050 | |
Tensile Strength | kg/cm 2 | 760 | |
Compressive Strength | kg/cm 2 | 1260 | |
ELECTRICAL | Didlectic Strength | Kv/mm | 20 |
Surface Resistivity | Ohm | > 10 16 | |
OPTICAL | Light Transmittance | % | 93 |
Refractive Index | - | ||
THERMAL | Specific Heat | Cal/grºC | 0.35 |
Coefficient of Thermal Cortductivily | Cal/xee/cm/ºC/cm | ||
Hot Forming Temp | ºC | 140-180 | |
Hot Defomation Temp | ºC | 100 | |
Thermal Expansion Coefficient | Cmfcm/V | 6×10-5 | |
MISCELLANEOUS | Water Absorption(24Hrs) | % | 0.3 |
Teste | % | None | |
Odor | |||