Audited Supplier
PVC011
ISO, CE
1.2mm
Waterproof Roll Material
Roll
PVC
PVC Ceilings
Anti-static, Heat Insulation, Waterproof
White
Outdoor, Indoor
Smooth
STAR FORCE
Paper Tube Inside Per Roll,Woven Bag,About 10000 S
1.2, 1.5, 1.8, 2.0
China
3920490090
Product Description
PVC waterproofing membrane is a high performance polymer waterproof sheets to PVC resin as the main raw material adding plasticizers, anti-UV agents, anti-aging agents, stabilizers and processing aids, by extrusion molding production polymer waterproofing membrane. Reliable product quality, convenient construction, various thickness, length, width can be customized according to customer requirements. As a result of this product over a unique formula, product life is far more than the general waterproof materials, long life of the entire water system, more than 20 years as roof waterproof material and more than 50 years if used in underground waterproof.
Note:
The above specifications are our regular sizes , the sizes could be ordered according to the customer's request. For more technical data sheet, please contact us.
Different Types:
Type H: Homogeneous PVC membrane.
Type L: PVC membrane backed with fabirc.
Type P: PVC membrane internally reinforced with fabric.
Type G: PVC membrane internally reinforced with glass fibers.
Type GL: PVC membrane internally reinforced with glass fibers and backed with fabric.
| Thickness | 1.2mm, 1.5mm, 1.8mm, 2.0mm |
| Width | 1.8m, 2.0m, or customized |
| Length | 20m or customized |
| Color | White, Gray or customized |
| Type | H / L / P Type |
| OEM | Available |
The above specifications are our regular sizes , the sizes could be ordered according to the customer's request. For more technical data sheet, please contact us.
Different Types:
Type H: Homogeneous PVC membrane.
Type L: PVC membrane backed with fabirc.
Type P: PVC membrane internally reinforced with fabric.
Type G: PVC membrane internally reinforced with glass fibers.
Type GL: PVC membrane internally reinforced with glass fibers and backed with fabric.
| No. | Item | H | L | P | G | GL | |
| 1 | The thickness of resin on reinforcement (mm) >= | --- | 0.4 | ||||
| 2 | Tensile strength | Max Tension strength (N/cm) >= | - | 120 | 250 | - | 120 |
| Tensile strength (Mpa) >= | 10.0 | - | - | 10.0 | - | ||
| Elongation at Max. tension (%)>= | - | - | 15 | - | - | ||
| Elongation at break (%) >= | 200 | 150 | - | 200 | 100 | ||
| 3 | Dimensional stability after heat treatment (%)<= | 2.0 | 1.0 | 0.5 | 0.1 | 0.1 | |
| 4 | Foldability at low temperature | -25ºC No cracks | |||||
| 5 | Watertightness | 0.3Mpa, 2H, impermeable | |||||