Virgin Pet Raw Material Granule
Bottles
CZ-328 CZ318
PP/PE Woven Bag or Paper Plastic Composite Bag
ISO9001
Accepted
Pet Granules
RPET Chips
Avaliable Sample
Food Grade
JTC
Jumbo / PP Woven Bag
25KG/1100KG JUMBO BAG
China
3907619000
Product Description
SPECIFICATION1. Virgin grade for water bottle
2.Resin chips
3.high quality with good price
4.100% virgin
Application: Bottle-grade polyester chips are suitable for making the packing bottles for pure water,
natural mineral water, distilled water, drinking water, flavoring and candy containers,
PET sheet material etc.
It is widely applied in various kinds of containers such as beverage bottles, edible oil bottles, condiment bottles, medicine
bottles, and PET sheet packaging bottles. Thanks to the unique process formula and manufacturing technology applied, the products
are featured with good crystallization property, low processing temperature and wide processing scope.
"JADE" bottle grade polyester chips are stable and reliable in product quality, and have been deeply trusted by our customers .
| Item | Unit | CZ-302 | CZ-302L | CZ-302A | CZ-318 | CZ-328 | CZ-328A | CZ-328H | CZ-333 |
| IV | DL/G | 0.8+/-0.015 | 0.78+/-0.015 | 0.8+/-0.015 | 0.83+/-0.015 | 0.875+/-0.015 | 0.87+/-0.015 | 0.89+/-0.015 | 0.8+/-0.015 |
| Cristallinity | % | 55+/-5 | 55+/-5 | 55+/-5 | 55+/-5 | 55+/-5 | 55+/-5 | 55+/-5 | 55+/-5 |
| Color | L- | ≥82 | ≥82 | ≥72 | ≥82 | ≥82 | ≥72 | ≥82 | ≥82 |
| B- | ≤1.0 | ≤1.0 | ≤0.0 | ≤1.0 | ≤1.0 | ≤0.0 | ≤1.0 | ≤1.0 | |
| COOH | Mmol/kg | ≤30 | ≤30 | ≤30 | ≤30 | ≤30 | ≤30 | ≤30 | ≤30 |
| AA | ppm Ug/g | ≤1.0 | ≤1.0 | ≤1.0 | ≤1.0 | ≤1.0 | ≤1.0 | ≤1.0 | ≤1.0 |
| DUST | ppm Mg/kg | ≤100 | ≤100 | ≤100 | ≤100 | ≤100 | ≤100 | ≤100 | ≤100 |
| Melting Point | ºC | 244+/-2 | 244+/-2 | 244+/-2 | 244+/-2 | 244+/-2 | 244+/-2 | 244+/-2 | 244+/-2 |
| Water Content | wt% | ≤0.4 | ≤0.4 | ≤0.4 | ≤0.4 | ≤0.4 | ≤0.4 | ≤0.4 | ≤0.4 |
| Wt.of100Chips | g | 1.40+/-0.10 | 1.40+/-0.10 | 1.40+/-0.10 | 1.40+/-0.10 | 1.40+/-0.10 | 1.40+/-0.10 | 1.40+/-0.10 | 1.40+/-0.10 |