Concrete, Filling Material, Spinning, Non-Woven Fabric, Replace Asbestos
Polyvinyl Alcohol
Anti-Pilling, Abrasion-Resistant, Flame Retardant, Anti-Distortion, Anti-Static, Heat-Resistant
Filament
Faint Yellow
High Strength Fiber
Miscellaneous Chain Synthetic
1500MPa
37gpa
6.5%
SAPEN
Bag+Pallet
D: 20/40um, L: 6-20mm
Shanghai, China
55039000
Product Description
Micro Synthetic PVA Fibre
(SAP 206S/ 212S)
DescriptionSAPEN monofilament PVA fiber is made of Polyvinyl alcohol. It's for use in fiber reinforced concrete, stucco and precast. PVA fiber is specifically designed for use in concrete products the surface is specially modified for the purpose of controlling plastic shrinkage, thermal cracking and improving abrasion resistance. When the fiber is used at high doses it can dramatically improve flexural characteristics of concrete products.
Application
- Replace asbestos use in cement products
- Slabs on ground
- Side-walks, driveways, decks, curbs
- Stucco and precast elements
- Overlays / toppings
- Tunnel shotcrete
- Roads / Pavements
- Bridge Decks
- Reduces the formation of plastic shrinkage cracking in concrete.
- Improves impact, shatter and abrasion resistance of concrete.
- Enhances durability and toughness of concrete
- Prevent water seepage and prolong the life of the building.
- Cost saving, easier to use,to disperse and safe to handle.
- Can be used in highly corrosive circumstance.
| Tensile Strength | >1500 MPa |
| Modulus | >37GPa |
| Elongation | 6.5±1% |
| Fibre dimension | Length: 6mm / 12mm ; Diameter:20/ 40μm |
| Melt Point | 230ºC |
| Density | 1.3g/cm3 |
| Acid&Alkali Resistance | Excellent |
| Reduction in 90ºC water | ≤1% |
| Appearance | Faint yellow |
| Safety | Non-toxic, non-irritating, neutral |
Guidelines for use
1. Generally, keep the original mix ratio and the stressed steel bar, no need to change.
2. Dosage: in general, about 0.9-1.9 kg/m3 of each cubic meter concrete.
3. Mixing: fibers can be added directly to the mixing system during or after the batching of the ingredients and mixed at high speed for a minimum of five minutes. Additional mixing does not adversely affect the distribution or overall performance of Fibers. The addition of Fibers at the normal or high dosage rate does not require any mix design or application changes. A water reducer or super-plasticizer is recommended in concrete products where improved workability and finishability are desired..
4. Forming and curing. No special requirements, just as usual.