Audited Supplier
C11000/SPHC/C11000
Strip
C11000/SPHC/F11/F18
Medium Carbon
Customize as Needed
Customize as Needed
Customize as Needed
Estar
Wood Pallet
GB/T
Ningbo
721260000
Product Description
iA copper-steel composite material with good elongation, high bonding strength, low resistivity, high tensile strength and low cost is provided. A copper-steel-copper composite material is disclosed. Its chemical composition proportion is 5-20% of copper and 80-95% of steel, and its structure is composed of copper and steel. The invention also discloses the preparation method of copper-steel composite material. The preparation steps are as follows: after surface treatment, copper and steel are rolled into high-precision steel strip and high-precision copper strip by cold rolling mill; after surface cleaning, surface residues are removed and degreased; high-precision copper-steel composite strip is rolled by cold rolling mill; and copper-steel composite strip is annealed at 650-850 C in vacuum furnace. In 1-4 hours, the structural molecules of the composite layer of two kinds of metal materials are melted, and then cooled to room temperature in vacuum furnace; the two kinds of strips are compounded to make the strips compounded into one and finish rolling; the composite materials are smoothed and polished, and the strips are packed after shearing according to the requirements of users.
Military industry: Copper-steel composite material temperature and pressure-penetration composite technology is a new technology emerging in the field of domestic metal composite strip materials, in addition to the high strength, good heat resistance, thermal stability, plasticity and corrosion resistance common to composite materials In addition to the characteristics of resistance and abrasion resistance, in the field of military bullet manufacturing, there are also the advantages of high yield and high dimensional accuracy, which are beneficial to improve the quality of bullets; the composite material has good consistency, thereby ensuring the consistency of the bullet and the shell; One batch is heavy and can be processed continuously, which greatly improves the production efficiency of bullets. The surface quality is excellent, comparable to pure copper; the brass on the surface of the copper-steel composite material also has a lubricating effect, which can reduce the impact on the barrel when shooting The wear and tear of the barrel and rim. It has been widely used in military products such as bullet shells and detonators. The sales network of military copper-steel composite materials has covered the world and won unanimous praise from many customers.
i)Military Products
ii)Chemical Composition
iii)Mechanical properties and metallographic structure
Equipment and workshop
Military industry: Copper-steel composite material temperature and pressure-penetration composite technology is a new technology emerging in the field of domestic metal composite strip materials, in addition to the high strength, good heat resistance, thermal stability, plasticity and corrosion resistance common to composite materials In addition to the characteristics of resistance and abrasion resistance, in the field of military bullet manufacturing, there are also the advantages of high yield and high dimensional accuracy, which are beneficial to improve the quality of bullets; the composite material has good consistency, thereby ensuring the consistency of the bullet and the shell; One batch is heavy and can be processed continuously, which greatly improves the production efficiency of bullets. The surface quality is excellent, comparable to pure copper; the brass on the surface of the copper-steel composite material also has a lubricating effect, which can reduce the impact on the barrel when shooting The wear and tear of the barrel and rim. It has been widely used in military products such as bullet shells and detonators. The sales network of military copper-steel composite materials has covered the world and won unanimous praise from many customers.
i)Military Products
| Standard size | Brass-steel-brass | Brass-steel-brass | Brass-steel-brass |
| Strip width | 139.5mm | 124/135/137/140mm | < 600 mm |
| Strip thickness | 1.7-3.6mm | 0.5-1.37mm | 0.05-4.0 mm |
| Coating thickness | 3.4%-4% | 3.4%-4% | 3%-15 % |
| Base material | F18 steel | F11 steel | SPHC steel |
| Cladding material | H90 copper | H90 copper | H90 copper |
| Delivery form | Coil / Strip | Coil / Strip | Coil / Strip |
ii)Chemical Composition
Grade
| Chemical composition of steel strip | ||||||||
C | Si | Mn | P | S | Ni | Cr | Cu | Als | |
% | % | % | % | % | % | % | % | % | |
F11 | ≤0.11 | ≤0.06 | 0.30-0.55 | ≤0.02 | ≤0.01 | ≤0.3 | ≤0.15 | ≤0.2 | 0.02-0.1 |
F18 | 0.11-0.19 | ≤0.06 | 0.35-0.55 | ≤0.02 | ≤0.01 | ≤0.3 | ≤0.15 | ≤0.2 | 0.02-0.1 |
SPHC | ≤0.15 | ≤0.05 | ≤0.6 | ≤0.035 | ≤0.035 | - | - | - | ≥0.010 |
Grade
| Chemical composition of copper strip | |||||||||
Cu+Ag (min) | P | Bi | Sb | As | Fe | Pb | S | Zn | Total impurities | |
% | % | % | % | % | % | % | % | % | % | |
H90 | 88-91 | - | - | - | - | ≤0.1 | ≤0.02 | - | allowance | ≤0.2 |
iii)Mechanical properties and metallographic structure
material | tensile strength(Mpa) | Elongation(%) | Grain size | Pearlite | Non-metallic inclusionsA/B/C/D | ||
Annealed | half hard | Annealed | half hard | ||||
H90/SPHC/H90 | 290~355 | 360~455 | ≥36% | ≥8% | 7-10 | 1-5 | ≤2.5 |
H90/F11/H90 | 265~365 | - | ≥43% | - | 7-10 | 1-5 | ≤2.5 |
H90/F18/H90 | 305~395 | - | ≥37% | - | 7-10 | 2-6 | ≤2.5 |