Product Description
Customerizd high performance PEEK CF30 CA30 solid Rods
| Material | Brand | Size (Rod) | Services | Application |
| PEEK | MBH | Dia. 4 /5/6/7/8/9/10/13/16/18/22/ 25/26/40/45/50/55/60/65/70/75 /80/85/90/100/130/160mm or customized Thickness 5mm-100mm sheet | sheet/rod extrusion and machining and plastic modified services | medical, pharmaceutical, and semi-conductor, Aerospace, Auto etc. |
Ketron® GF30 Polyetheretherketone PEEK is a 30% glass fiber reinforced grade with excellent dimensional stability and outstanding chemical, corrosion, and creep resistance. With the addition of glass fibers, Ketron® GF30 PEEK has a significantly low expansion rate and high flexural modulus. In addition to these cPEEK CF 30 is a 30% carbon filled PEEK material that is manufactured by Ensinger under the tradename TECAPEEK CF30 black. Its carbon fibre reinforcement lends the material a high level of rigidity and creep strength. Carbon fibre reinforced PEEK demonstrates very high mechanical strength values, while exhibiting lower density than 30% glass fibre filled peek. Furthermore, carbon fibre composites tend to be less abrasive than glass fibres while simultaneously resulting in improved wear and friction properties. The addition of carbon fibres also ensures a significantly higher level of heat conductivity which is also beneficial for increasing part life in sliding applications. Carbon filled PEEK has also an excellent resistance to hydrolysis in boiling water and superheated steam.
| Typical Properties | Test standard | Unit | Value | |
| Physical | ||||
| Colour | black | |||
| Density | ISO 1183-1 | g/cm3 | 1.40 | |
| Water Aborption | 23ºC, 50%RH | ISO 62 | - | 0.16 |
| Thermal | ||||
| Thermal conductivity at 23ºC | ISO 11359 | 10^-5/K | 10.00 | |
| Max. material working Temperature(Rti) | UL 746B | ºC | 240.00 | |
| Melting point Tm | DSC | ºC | 343.00 | |
| Glass transition temperature Tg | DSC | ºC | 143.00 | |
| Form stability Tm.HDT/ A1.8 Mpa | Din EN ISO 75 | ºC | 336.00 | |
| Mechnical | ||||
| tension Test | Tensile Strength at break | DIN EN ISO 527 | MPa | 260.00 |
| elongation at break | DIN EN ISO 527 | % | 1.70 | |
| bending strength | DIN EN ISO 178 | MPa | 380.00 | |
| Compressive strength | DIN EN ISO 604 | MPa | 250.00 | |
| Charpy Impact Strength (no notch) | EN ISO 179 | kJ/m^2 | 45.00 | |
| Charpy Impact Strength (with notch) | EN ISO 179 | kJ/m^2 | 7.00 | |
| shore Hardness | ISO 868 | Scale D | 88.00 | |
| Electrical | ||||
| Electrical Resistivity | DSC | j/(kg*K) | 1800 | |
| PV value at V=0.5 m/s(30 m/min) | IEC 60093 | Ω*cm | 1.0E5 | |
| others | ||||