Audited Supplier
FX-808
25135-73-3
C22h26o10
White
Powder Coating
Good Adhesion,Good Weather Resistance
Greater Than or Equal to 66
48-55mgkoh/G
2800-3800cps
200ºC/10min
White Particles
90/10
Powder Coating Resins
AQUACITY
One Ton /Pallet
25KG/bag
China
3907999990
Product Description
| Curing Agent | Triglycidyl Isocyanurate(TGIC) | |||||||
| Hydroxy alkyl amide(HAA) | ||||||||
| Type of Resins | Item No. | Ratio PE/Crosslinker | Acid Value (mgKOH/g) | Viscosity(p/200ºC) /mpa.s | Tg Value (°C) | Cure cycle ºC/min | Key Features | |
| TGIC Based Polyester Resins | FX-902 | 93/7 | 30~35 | 4000~5000 | ≥64 | 200*10 | High gloss ,Excellent flow, weathering resistance and mechanical properties | |
| FX-903 | 93/7 | 30~35 | 4500~5500 | ≥62 | 200*10 | Super weathering resistance, Excellent mechanical properties,good flow | ||
| FX-906 | 93/7 | 30~35 | 4000~5000 | ≥65 | 200*10 | High gloss ,Excellent flow, boiling water resistance, mechanical properties | ||
| FX-907 | 93/7 | 29~35 | 5000~6000 | ≥67 | 200*10 | Good weathering resistance and mechanical properties,,suitable for texture powder coating | ||
| FX-801 | 96/4 | 18~24 | 5500~6500 | ≥65 | 200*10 | For dry blend matte system as fast component,good storage stability | ||
| FX-802 | 93/7 | 30~36 | 3800~4800 | ≥65 | 200*10 | Excellent flow,suitable for High gloss and matt | ||
| FX-808 | 90/10 | 48~55 | 2800~3800 | ≥66 | 200*10 | For dry blend matte system as fast component,good storage stability | ||
| FX-301 | 96/4 | 18~24 | 5000~6000 | ≥65 | 200*10 | Low cost resin,for dry blend matte system as fast component,good storage stability | ||
| FX-303 | 93/7 | 30~36 | 3600~4600 | ≥64 | 200*10 | Low cost resin,good flow and mechanical properties | ||
| FX-307 | 93/7 | 30~35 | 4800~6000 | ≥65 | 200*10 | Low cost resin,suitable for texture powder coating | ||
| FX-308 | 90/10 | 50~56 | 2600~3600 | ≥65 | 200*10 | Low cost resin,for dry blend matte system as fast component,good storage stability | ||
| Primid(HAA) Based Polyester Resins | FX-H602 | 95/5 | 20~25 | 4000~5000 | ≥64 | 180*15 | Low cost resin,good flow and mechanical properties | |
| FX-H604 | 96.5/3.5 | 18~24 | 6000~7500 | ≥61 | 180*15 200*10 | Low cost resin,based on hydroxy alkyl amide (HAA) ,good flow ,good overbake resistance to yellowing | ||
AQUACITY FX-808
| Product Name | Powder Coating Polyester Resin | ||||
| Product Model | FX-808 | ||||
| Product Description | FX-808 is high and low acid value polyester resin. For polyester/TGIC curing powder coating system. After being made into powder by C808, it can be dry mixed to make outdoor semi gloss powder coating, which has low luster, good weather resistance and leveling property. | ||||
| Product appearance | White particles | ||||
| Viscosity (200 ° C,mpa.s) | 2800~3800 | ||||
| Acid Value(mgKOH/g) | 48-55 | ||||
| Glass Transition Temperature | ≥66 | ||||
| Curing Ratio | 90/10 |
EXTRUSION AND APPLICATION CONDITIONS
| Squeeze | |||||||
| Screw | 40HZ | ||||||
| Zone 1 temperature | 105 | ||||||
| Zone 2 temperature | 110 | ||||||
| Application | |||||||
| Film thickness, substrate | 60-80um film thickness, 0.5mm cold rolled steel plate | ||||||
| Gloss | <25% | ||||||
| Recoil(kg.cm) | 50 | ||||||
| Foreflush(kg.cm) | 50 | ||||||
| Adhesion(grade) | 0 | ||||||
| Foshan Faxus New Material Company Limited |
| Please be noticed that the information and testing results represent above is for reference only. Results and figures above will be changed based on different testing conditions. Customers are suggested to design and test the product formula based on the actual conditions of production properties. |
STORAGE CONDITION
- Storage temperature ≤ 30ºC;
- Storage condition is required to be dry and with good air circulation.
- Avoiding sunlight exposure.
PACKAGE
The products are packed by polyethylene bag, 25kg/bag, 1ton/pallet.