Chopped Strand Fiberglass Mat (CSM)
Facing (Surfacing) Mat
E-Glass
3200mm
13 Micron
JLON
PE Bag
80-900gsm
Changzhou, China
70193100
Product Description
If you search for Hand Lay-up products, we can provide not only chop strand mat, but also woven roving, you can read below related products for reference.
Chopped Strand Mat:
Chopped strand mat is produced by chopping continuous roving into length of 5cm and randomly dispersing the cut fibers. These fibers are held together by powder or emulsion binder. It is typically used for hand lay up process. The mats are compatible with unsaturated polyester, vinyl ester and PU resins. Width ranges from 50mm to 3200mm.
Application: panels, tanks, boats, complete set of sanitary equipment, automotive parts, cooling towers, pipes etc
Specifications:
Related product-Woven roving
Introduction:
Fiberglass Woven Roving is bidirectional fabric made by interweaving direct roving. Can be compatible with unsaturated polyester, vinyl ester, epoxy and phenolic resins. With high-performance reinforcement, widely used in hand lay up to manufacture boats, vessels, plane and automotive parts, furniture and sports facilities. The area weight is from 200g/m2 to 1200g/m2. The width is from 50mm-3000mm.
Specifications:
Chopped Strand Mat:
Chopped strand mat is produced by chopping continuous roving into length of 5cm and randomly dispersing the cut fibers. These fibers are held together by powder or emulsion binder. It is typically used for hand lay up process. The mats are compatible with unsaturated polyester, vinyl ester and PU resins. Width ranges from 50mm to 3200mm.
Application: panels, tanks, boats, complete set of sanitary equipment, automotive parts, cooling towers, pipes etc
Specifications:
| Item | Weight(g/m2) | Binder Content(%) | Water Content(%) |
| EMC100 | 100 | 9-12 | <0.2 (powder bonded) <0.5 (emulsion bonded) |
| EMC150 | 150 | 9-12 | <0.2 (powder bonded) <0.5 (emulsion bonded) |
| EMC225 | 225 | 2-8 | <0.2 (powder bonded) <0.5 (emulsion bonded) |
| EMC300 | 300 | 2-8 | <0.2 (powder bonded) <0.5 (emulsion bonded) |
| EMC450 | 450 | 2-8 | <0.2 (powder bonded) <0.5 (emulsion bonded) |
| EMC600 | 600 | 2-8 | <0.2 (powder bonded) <0.5 (emulsion bonded) |
Related product-Woven roving
Introduction:
Fiberglass Woven Roving is bidirectional fabric made by interweaving direct roving. Can be compatible with unsaturated polyester, vinyl ester, epoxy and phenolic resins. With high-performance reinforcement, widely used in hand lay up to manufacture boats, vessels, plane and automotive parts, furniture and sports facilities. The area weight is from 200g/m2 to 1200g/m2. The width is from 50mm-3000mm.
Specifications:
| Product No. | Glass | Weight(g/m²) | Breaking Strength ≥N/25MM | Weave | Moisture Content % | L.O.I Content % | |
| Warp | Weft | ||||||
| WR200 | E | 200+/-10 | 820 | 700 | Plain | ≤0.1 | 0.4-0.8 |
| WR270 | E/ECR | 270+/-14 | 1200 | 1000 | Plain | ≤0.1 | 0.4-0.8 |
| WR300 | E | 300+/-15 | 1200 | 1200 | Plain | ≤0.1 | 0.4-0.8 |
| WR360 | E/ECR | 400+/-20 | 1200 | 1150 | Plain | ≤0.1 | 0.4-0.8 |
| WR400 | E | 400+/-20 | 1480 | 1380 | Plain | ≤0.1 | 0.4-0.8 |
| WR500T | E | 500+/-25 | 1800 | 1700 | Twill | ≤0.1 | 0.4-0.8 |
| WR500 | E | 500+/-25 | 1800 | 1600 | Plain | ≤0.1 | 0.4-0.8 |
| WUDT500 | E | 500+/-25 | 100 | 2900 | Plain | ≤0.1 | 0.4-0.8 |
| WUDL500 | E | 500+/-25 | 2600 | 350 | Plain | ≤0.1 | 0.4-0.8 |
| WUDL530 | E | 530+/-27 | 3200 | 800 | Plain | ≤0.1 | 0.4-0.8 |
| WR580 | E/ECR | 580+/-29 | 1900 | 1600 | Plain | ≤0.1 | 0.4-0.8 |
| WR600 | E | 600+/-30 | 1900 | 1800 | Plain | ≤0.1 | 0.4-.8 |
| WR600B | E | 600+/-30 | 1900 | 1850 | Plain | ≤0.1 | 0.4-0.8 |
| WUDL600 | E | 600+/-30 | 3100 | 350 | Plain | ≤0.1 | 0.4-0.8 |
| WR800 | E | 800+/-40 | 2600 | 2300 | Plain | ≤0.1 | 0.4-0.8 |
| WR800A | E | 864+/-43 | 2900 | 2700 | Plain | ≤0.1 | 0.4-0.8 |
| WR1000 | E | 1000+/-50 | 2900 | 2900 | Plain | ≤0.1 | 0.4-0.8 |