Product Description
3240is a laminated board prepared from alkali-free E-glasscloth impregnated with epoxy phenolic resin by pressing under high temperature and pressure. The 3240 cn be used in many electric fields and in humidity environment and in transformer oil.
Features:
1. High mechanical properties, its flexural strength(MR) are over 4000kgf/cm2
2. High dielectric properties
3. High adhesion strength
4. High thermal resistance.
5. High moisture resistance.Product Description
3240 epoxy fiber glass cloth laminated sheet /epoxy resin sheet is made by impregnating an alkali-free E glass cloth into epoxy resin and phenolic resin, then baking and hot pressing under high temperature and high pressure environment.
Relevant Product Parameters
Features:
1. High mechanical properties, its flexural strength(MR) are over 4000kgf/cm2
2. High dielectric properties
3. High adhesion strength
4. High thermal resistance.
5. High moisture resistance.
Product Description
3240 epoxy fiber glass cloth laminated sheet /epoxy resin sheet is made by impregnating an alkali-free E glass cloth into epoxy resin and phenolic resin, then baking and hot pressing under high temperature and high pressure environment.
| Name | 3240 epoxy fiber glass cloth laminated sheet /epoxy resin sheet | Size | 1020*1220mm,1020*2040mm,1220*2040mm,1220*2440mm |
| Thickness | 0.2-100mm | Color | Yellow |
| Density | 2.06 g/cm3 | Component | Epoxy resin + Glass fiber cloth |
| Item | Unit | Index value |
| Vertical bending strength | MPa | ≥340 |
| Parallel impact strength (simply-supported beam method) | KJ/ | ≥33 |
| Parallel impact strength (cantilever beam method) | KJ/ | ≥34 |
| Vertical electric strength (in oil of 90ºC±2ºC,1mm) | MV/m | ≥14.2 |
| Parallel breakdown voltage (in oil of 90ºC±2ºC) | KV | ≥35 |
| Dielectric constant (below 48Hz-62Hz) | - | ≤5.5 |
| Dielectric constant (below 1MHz) | - | ≤5.5 |
| Thermostability | ºC | 150 |
| Oil resistivity in transformer oil 4h | ºC | 130 |
| Tensile strength lengthways horizontal | MPA | ≥314 |
| Adhesive strength | N | ≥5600 |
| Dielectric dissipation factor (below 48Hz-62Hz ) | - | ≤0.04 |
| Dielectric dissipation factor (below 1MHz ) | - | ≤0.04 |
| Density | g/ cm3 | (1.8-2) |