FRP Fiber Reinforced Polymer / Plastic Rod

Glass fiber Rod for optical cables
FRP: Fiber Reinforced Polymer/Plastic
Glass fiber reinforced core for optical cables
1, Round FRP from Dia0.90mm to Dia5.00mm
  Specifications: Diameters from 0.90mm to 5.00mm.
  Roll Length from 15kms to 50kms with no joints.
  Minimum Tensile strength:1100mpa
  Minimum Tensile Modulus: 50mpa.
  Minimum Flexural Strength: 1100mpa.
  Minimum Flexural Modulus: 50mpa.
  Maximum Elongation at break: 4%
  Coefficient of linear thermal expansion(from -30ºC to 80ºC): Max 8x10^-6/ºC
  Diameter Tolerance: +/-2%
  Minimum Bending Radius:40xD mm.
  Density: 2.05 --2.15g/cm3
  High Temperature Bending Test(50ºC,100ºC,120h): No bur, cracks or breaks.
 2, Round FRP Dia0.40mm & Dia0.50mm
  Specifications: Diameters 0.40mm & 0.50mm.
  Roll Length from 25kms to 50kms with no joints.
  Minimum Tensile strength:1280mpa
  Minimum Tensile Modulus: 46mpa.
  Minimum Flexural Strength: 1100mpa.
  Minimum Flexural Modulus: 50mpa.
  Maximum Elongation at break: 3%
  Coefficient of linear thermal expansion(from -30ºC to 80ºC): Max 8x10^-6/ºC
  Diameter Tolerance: +/-2%
  Minimum Bending Radius:18xD mm.
  Density: 2.05 --2.15g/cm3
  High Temperature Bending Test(80ºC,24h): Minimum 38xDmm
3, Flat FRP from 0.6X1.3mm to 10x3mm.
  Specifications: from flat 0.6x1.3mm to 10x3mm.
  Roll Length from 5kms to 50kms with no joints.
  Minimum Tensile strength:1200mpa
  Minimum Tensile Modulus: 48mpa.
  Maximum Elongation at break: 3%
  Tolerance of both Width and Thickness: +/-2%
  Minimum Bending Radius:30xT mm.
  Density: 2.05 --2.15g/cm3
  High Temperature Bending Test(100ºC,24h):Minimum 8xT mm.