Audited Supplier
Hiperco 50A(1j22) alloy is a soft magnetic alloy which has been used primarily as magnetic core material in electrical core material in electrical equipment requiring high permeability values at very high magnetic flux densities. The magnetic characteristics of this alloy permit weight reduction, reduction of copper turns, and insulation in the end product when compared to other magnetic alloys having lower permeabilities in the same magnetic field range.
AFK502 and Hiperco 50A strip is similar with Chinese 1J22 (GB/T 15002-1994)
Note: We could do any other products with specified technical standard, say, ASTM,SAE,DIN,S.E.W.,JIS,ISO,IEC,NF,BS.
Grade | U.K. | Germany | U.S.A. | Russia | Standard |
Hiperco 50A AFK502 | Permendur | Vacoflux 50 | Supermendur HiperCo50 | GB/T15002-1994 |
Chemical Composition (%) | |||||||||
C≤ | Mn≤ | Si≤ | P≤ | S≤ | Cu≤ | Ni≤ | Co | V | Fe |
0.04 | 0.30 | 0.30 | 0.020 | 0.020 | 0.20 | 0.50 | 49.0~51.0 | 0.80~1.80 | Balance |
Physical Property (see Table2 ) Table 2 Physical Property | |||||
Resistivity /(μΩ•m) | Density/(g/cm3) | Curie point/°C | Magnetostriction Cofficient/(×10-6) | Tensile Strength,N/mm2 | |
Unannealed | Annealed | ||||
0.40 | 8.20 | 980 | 60~100 | 1325 | 490 |
Table 3 DC Magnetic Property Requirements After Heat-Treated | |||||||
Type | Minimum Magnetic Flux Density for Different Magnetic Field Strengths (T) | Coercive force Hc / (A/m)≤ | |||||
B400 | B800 | B1600 | B2400 | B4000 | B8000 | ||
Cold rolled Strips | 1.70 | 1.90 | 2.00 | 2.10 | 2.20 | 2.25 | 110 |
Wires,Forgings,Billets,Bars | 1.60 | 1.70 | 1.80 | 2.05 | 2.15 | 2.20 | 144 |
Soft magnetic alloys are a class of alloys with high permeability and low coercivity in weak magnetic fields. According to the different elements that make up the alloy, it can be divided into electromagnetic pure iron (industrial pure iron), iron-silicon alloy, iron-nickel alloy, iron-aluminum alloy, iron-silicon-aluminum alloy and iron-cobalt alloy, etc.1J06,1J12,1J17,1J18,1J22,1J30,1J36,1J38,1J46,1J50,1J51,1J54,1J76,1J77,1J79,1J80,1J85,1J87
Permanent magnet alloy not only has high hardness and mechanical properties, but also has strong anti-demagnetization ability, high coercivity value (greater than 20kA/m), magnetic "hard" and other characteristics, so it is also called hard magnetic alloy.2J04,2J07,2J09,2J10,2J31,2J53,2J84,2J85Elastic alloys include high elastic alloys and constant elastic alloys. It is used to make elastic elements such as elastic sensitive elements, energy storage elements and frequency elements in precision instruments.3J01,3J21,3J53Expansion alloys(Invar Alloy) are divided into Kovar alloys, ceramic sealing alloys, low expansion alloys, and constant expansion alloys. Widely used in electronic industry, precision measuring tools, precision instruments and low temperature engineering and other fields.4J28,4J29,4J32,4J33,4J36,4J40,4J42,4J50
Precision alloys with nickel, chromium, aluminum and iron as the main components, the resistivity is about three times higher than that of manganese copper, and has a lower temperature coefficient of resistance and low thermal potential to copper, with good long-term resistance stability and resistance. Oxidation properties.
It is suitable for making precision resistance elements in various measuring instruments and meters, making precision micro-resistance elements and strain gauges.6J10,6J15,6J20,6J22,6J23,6J24
| expansion alloy | ||||||||||
| Grade | C≤ | S≤ | P≤ | Mn | Si | Ni | Cr | Cu | Al | Fe |
| 6J10 | ≤0.05 | ≤0.01 | ≤0.01 | ≤0.3 | ≤0.2 | nI+cO rem | 9-10 | ≤0.2 | ≤0.4 | |
| 6J15 | ≤0.05 | ≤0.02 | ≤0.03 | ≤1.5 | 0.4-1.3 | 55-61 | 15-18 | ≤0.3 | rem | |
| 6J20 | ≤0.05 | ≤0.01 | ≤0.01 | ≤0.7 | 0.4-1.3 | rem | 20-23 | ≤0.3 | ≥1.5 | |
| 6J22 | ≤0.04 | ≤0.01 | ≤0.01 | 0.5-1.5 | ≤0.2 | rem | 19-21.5 | 2.7-3.2 | 2-3 | |
| 6J23 | ≤0.04 | ≤0.01 | ≤0.01 | 0.5-1.5 | ≤0.2 | rem | 19-21.5 | 2-3 | 2.7-3.2 | |
| 6J24 | ≤0.04 | ≤0.01 | ≤0.01 | 1.0-3.0 | 0.9-1.5 | rem | 19-21.5 | 2.7-3.2 | ≤0.5 | |
Constantan alloy
Manganese Copper Alloy
| Brand | Ni | Mn | Cu | |
| Constantan alloy | 6J40 | 39-41 | 1-2 | Rest |
| Manganese Copper Alloy | 6J12 | 2-3 | 11-13 | Rest |
Our company Principle is " Quality first, Customer first".
CHANGZHOU DLX ALLOY CO, LTD was established in 2002 and has got Iso9001 International Quality Management System Certificate and SGS Certificate. Our factory is professional in researching and producing special alloy material. From melting, drawing, heat treatment, finishing and testing .We offer nickel-based, copper-based, and iron-based alloys, including super alloy, welding materials, anti-corrosion alloy, precision alloy, FeCrAl alloy, NiCr alloy, CuNi alloy, thermocouple and etc, in the form of wire, strip, ribbon, bar, tube, plate.
DLX alloy, which is a alloy factory more than 18 years, we are founded in 2002, and run business with resistance alloy first. And in past 20 years, we R&D new product such as Thermocouple alloy,inconel, monel, hastelloy, high temperature alloy and other nickel based alloy products.
What is your working time?
Monday-Friday : 8:30AM-17:00PM (Beijing time, GMT+08.00)
We have public holiday during May.1-3, Oct.1-7 and Chinese New Year holiday . Pls e-mail us during our holiday if u have any questions.
Do you provide free samples?
Yes, we can provide a free sample for testing,buyer should bear the shipping costs.
What is your payment terms?
T/T,L/C,D/A,D/P,Western Union,MoneyGram,Paypal
What is the lead time?
Usually sample lead time is 15 days after payment has been confirmed.