Product Description
Product introduction:
With the development of automobile, tractor manufacturing industry and large-scale mining equipment, the size and weight of heat-treated parts are increasing. In order to improve production efficiency, the quenching amount of primary parts is increasing, and continuous quenching automatic line is emerging, which leads to the development of high speed quenching oil. Fast quenching oil is quenching oil with additives added, and the cooling speed is faster than ordinary quenching oil. When quenching with conventional quenching oil, problems such as soft spots, low hardness, poor hardening depth always occur in thick and large workpieces or poor hardenability workpieces. KERUN KR218H fast quenching oil can avoid the above problems and obtain high and even surface hardness and enough hardening depth.
Kerun's fast quenching oil has strong cooling capacity, high temperature cooling speed and moderate low temperature cooling speed, which can not only make the workpieces obtain high and uniform surface hardness and enough hardening layer depth, but also can better control the quenching deformation, and the surface of the workpieces after quenching is easy to clean, with good thermal oxidation stability and long service life.
Product Features:
Product Parameter:
With the development of automobile, tractor manufacturing industry and large-scale mining equipment, the size and weight of heat-treated parts are increasing. In order to improve production efficiency, the quenching amount of primary parts is increasing, and continuous quenching automatic line is emerging, which leads to the development of high speed quenching oil. Fast quenching oil is quenching oil with additives added, and the cooling speed is faster than ordinary quenching oil. When quenching with conventional quenching oil, problems such as soft spots, low hardness, poor hardening depth always occur in thick and large workpieces or poor hardenability workpieces. KERUN KR218H fast quenching oil can avoid the above problems and obtain high and even surface hardness and enough hardening depth.
Kerun's fast quenching oil has strong cooling capacity, high temperature cooling speed and moderate low temperature cooling speed, which can not only make the workpieces obtain high and uniform surface hardness and enough hardening layer depth, but also can better control the quenching deformation, and the surface of the workpieces after quenching is easy to clean, with good thermal oxidation stability and long service life.
Product Features:
1.Short vapor film stage, fast cooling at high and medium temperature stage, and has an appropriate cooling at low temperature stage.
2.For medium and large workpieces, high and uniform surface hardness and enough hardened depth can be obtained, and the deformation of workpiece can also be well controlled.
3.Good thermal oxidation stability, long service life.
4.Stable, low oil consumption and low use cost.
Product Parameter:
| Item | KR218H | Method |
| Moisture, ≤ | 0.03% | ASTM D6304 |
| Flash point (open cup), ≥ | 175°C | ASTM D92 |
| Kinematic viscosity (40°C) | 14-24 mm2/s | ASTM D7279 |
| Corrosion (Copper sheet 100°C×3h), ≤ | 1 | ASTM D130 |
| acid value, ≤ | 0.3 mgKOH/g | ASTM D664 |
| Thermal oxidation stability, viscosity ratio, ≤ | 1.25 | SH/T 0219 |
| Cooling performance Characteristic temperature | ≥680°C | ISO 9950 |
| 60°C, static Max. typical cooling rate | 105°C /s |