Phenolic Fiberglass Molding Plastics
This series of products are thermosetting molding plastics made of e-glass fiber and modified phenolic resin by soaking and baking. It is used for pressing heat-resistant, moisture-proof, mildew proof, high mechanical strength, good flame retardant insulating parts, but also according to the requirements of the parts, the fiber can be properly combined and arranged, with high tensile strength and bending strength, and suitable for wet conditions.
- Mechanical Excellence: Our product boasts excellent mechanical properties, ensuring durability and reliability.
- Electrical Insulation: With superior electrical insulation, our product guarantees safety and efficiency.
- Arc Resistance and Anti-Static: Designed to resist arcs and prevent static buildup, our product ensures a secure and stable performance.
- Corrosion Resistance: Our product exhibits outstanding resistance to corrosion, making it suitable for use with acid, alkali solutions, and other chemicals.
- Lightweight and High Product Utilization: Weighing less and offering high product utilization, our product optimizes efficiency and reduces costs.
- Strong Designability: Our product allows for versatile and flexible designs, meeting various application requirements.
- Widely Used: Our product finds extensive applications across industries due to its exceptional properties and reliability.
| NO. | Test ltem | Unit | Index | Test |
| 1 | Resin Content | % | Customized | 39 |
| 2 | Volatile Matter Content | % | 4.0-8.5 | 6 |
| 3 | Density | g/cm3 | 1.65-1.85 | 1.85 |
| 4 | Moisture Content | mg | ≤20 | 18 |
| 5 | Martens Temperature | ºC | ≥280 | 280 |
| 6 | Bending Strength | Mpa | ≥160 | 415 |
| 7 | Tensile Strength | Mpa | ≥80 | 160 |
| 8 | Dielectric Strength | MV/m | ≥14.0 | 18 |
| 9 | Charpy Impact Strength | KJ/m2 | ≥50 | 120 |
| 10 | Surface Resistivity | Ω | ≥1.0x10^12 | 2.0*10^13 |
| 11 | Volume Resistivity | Ω.m | ≥1.0x10^10 | 2.6*10^12 |
| 12 | Flexural Modulus | Gpa | 32.4 | 33 |
It is suitable for pressing mechanical components with high strength, electrical components with complex shape, radio parts, mechanical parts and electrical parts with high strength and commutator (commutator), etc. Its products also have good electrical performance, especially suitable for hot and humid areas.
It should be stored in a dry and ventilated room where the temperature does not exceed 30ºC.
Do not close to fire, heating and direct sunlight, erect stored on a special platform, horizontal stacking and heavy pressure are strictly prohibited.
Shelf life is two months from the date of production. After the storage period, the product can still be used after passing the inspection according to the product standards. Technical standard: JB/T5822-2015