Rated temperature:-60ºC~+180ºC
Short term temperature:+220ºC ≤12h
Instantaneous load temperature:1~5sec. +350ºC
Conductor: tinned copper wire soft core
Semi conductive strip
Silicon rubber insulation
Woven glass fiber silicone resin coatings
ITEMS | Technical Datas | Applied Standard | ||
Outer appearance | Smooth even without loose | UL758 JB 6213.4-2006 Q/320281ANX01-2012 GB 5013.3-2008 DINISO 34-1 | ||
Spark test | 31KV/15 min | |||
Breakdown voltage | 50KV | |||
Minimum bending radius | 6×d | |||
insulation mechanical character | Before aging | Tensile strength | ≥7.0N/mm² | |
Elongation at break | ≥250% | |||
Tearing strength | 30N/ mm | |||
Hardness | 65~70A | |||
After aging (200±3ºC×240h) | Tensile strength | ≥5.0N/mm² | ||
Elongation at break | ≥150% | |||
Hot ductility test Test conditions:200ºC 15 min | Load elongation | ≤175% | ||
Cooling of the largest permanent elongation | ≤25% | |||
harmful substance control | COMPLY WITH ROHS | EU-2002/95/EC | ||
Spec | Conductor | Wire diameter | Max Resistance | ||
The maximum diameter of filament | Diameter | Nominal | Tolerance | ||
mm² | mm | mm | mm | ||
4.0 | 0.31 | 2.7 | 10.40 | ±0.60 | 5.09 |
6.0 | 0.31 | 3.5 | 11.20 | ±0.60 | 3.39 |
10.0 | 0.41 | 4.6 | 12.70 | ±0.60 | 1.95 |
16.0 | 0.41 | 5.6 | 13.80 | ±0.60 | 1.24 |
25.0 | 0.41 | 7.1 | 15.30 | ±0.80 | 0.795 |
35.0 | 0.41 | 8.3 | 16.50 | ±0.80 | 0.565 |
50.0 | 0.41 | 10.0 | 18.60 | ±0.80 | 0.393 |
70.0 | 0.51 | 12.0 | 20.70 | ±1.0 | 0.277 |
95.0 | 0.51 | 14.0 | 22.70 | ±1.0 | 0.210 |
120.0 | 0.51 | 15.8 | 24.50 | ±1.0 | 0.164 |
150.0 | 0.51 | 17.7 | 26.80 | ±1.0 | 0.132 |
185.0 | 0.51 | 19.7 | 28.80 | ±1.0 | 0.108 |
240.0 | 0.51 | 22.6 | 32.20 | ±1.2 | 0.0817 |
300.0 | 0.51 | 25.2 | 35.20 | ±1.2 | 0.0654 |
400.0 | 0.51 | 29.2 | 39.20 | ±1.2 | 0.0495 |