Product Description
DESCRIPTION
HDPE FI0750 is a high molecular High Density Polyethylene copolymer grade typically used for blown film applications. HDPE FI0750
features are balance between toughness and stiffness, good impact properties with low gel level.
This product is not intended for and must not be used in any pharmaceutical/medical applications.
TYPICAL APPLICATIONS
HDPE FI0750 is typically used for blown film extrusion. Typical applications are heavy duty bags, grocery sacks, shopping bags, refuse bags, liners
for multi-wall sacks and liners for frozen food meat. The grade can be blended with LLDPE and LDPE and can be used in co-extrusion process.
Packaging:In 25kg bag, 26-28MT in one 40HQ.
| No. | Properties | Value (SI Units) | Method |
| 01 | Density | 0.946 g/cm3 | ASTM D1505 |
| 02 | Melt Index, Condition 190°C / 2.16 kg | 0.18 g/10 min | ASTM D1238 |
| 03 | Brittleness Temperature, Type A clamp, Type I specimen | <-75°C | ASTM D746 |
| 04 | ESCR, Condition B (100% Igepal), F50 | >1000 hrs | ASTM D1693 |
| 05 | Flexural Modulus, Tangent - 16:1 span:depth, 12.7 mm/min | 1150 MPa | ASTM D790 |
| 06 | Dart Drop (66 cm) | 90 g | ASTM D1709 |
| 07 | Tensile Strength at Yield, 50.8 mm/min MD | 24 MPa | ASTM D882 |
| 08 | Tensile Strength at Yield, 50.8 mm/min TD | 26 MPa | ASTM D882 |
| 09 | Elongation at Break, 50.8 mm/min MD | 480% | ASTM D882 |
| 10 | Elongation at Break, 50.8 mm/min TD | 640% | ASTM D882 |
| 11 | Elmendorf Tear Strength, MD | 19 g | ASTM D1922 |
| 12 | Elmendorf Tear Strength, TD | 270 g | ASTM D1922 |