Blast Furnace, Cement Kiln, Ceramic Kiln, Chemical Kiln, Glass Kiln, Steel-Making Furnace
Mullite
1580< Refractoriness< 1770
Extrusion Method
0.6g/cm3
40%
vuulcan
Sea-Worthy Wooden Case
customized
China
Product Description
The JM series lightweight heat insulation bricks have a bulk weight of 0.6 to 1.25g/cm3 and a service temperature range of 1300 ° C to 1600 ° C, and each grade has a unique design to meet different thermal, physical and chemical requirements. GM series light insulation bricks are made of high quality ultra-pure raw materials, and the packing is strictly classified according to the grade. These fillers are fired during the manufacturing process to form a uniform pore structure. Each face of the brick is machined to the exact dimensions required. This material benefits by reducing fuel costs, construction costs, and time spent in high temperature furnaces.Application of heat-insulating firebrickNon-ferrous furnace
Rotary kiln and shaft kiln
All kinds of incinerators
Heating furnace
Permanent lining of electric arc furnace ladle
General industrial furnace, etc
Characteristics of heat-insulating firebrick
Mechanical strength
hyperthermia
Excellent resistance to spalling
Corrosion resistance
Excellent load bearing performance
| Brand Properties | JM-23LD | JM-23 | JM -26 | JM -28 | JM -30 | JM -32 | |
| Classification temperature (ºC) | 1300 | 1300 | 1400 | 1500 | 1550 | 1600 | |
| Bulk Density (g/cm3) | 0.55 | 0.6 | 0.8 | 0.9 | 1.0 | 1.1 | |
| Cold Crushing Strength (MPa) | 1.0 | 1.2 | 1.8 | 2.5 | 3.3 | 3.5 | |
| Modulus of rupture (MPa) | 1.0 | 1.0 | 1.7 | 2.3 | 3.1 | 3.2 | |
| (CTºCX24h) Permanent Linear Change (%) | -0.4 | 0.6 | 0.6 | 0.8 | 0.9 | 1.01 | |
| Thermal Linear Expansion(%) @ 1,100ºC | 0.50 | 0.50 | 0.52 | 0.52 | 0.53 | 0.7 | |
| Thermal conductivity (W/m.k) | 350ºC | 0.14 | 0.18 | 0.27 | 0.32 | 0.38 | 0.49 |
| Chemical Analysis (%) | 400ºC | 0.15 | 0.20 | 0.29 | 0.34 | 0.40 | 0.5 |
| 600ºC | 0.17 | 0.24 | 0.32 | 0.36 | 0.42 | 0.51 | |
| Al2O3 | 38 | 40 | 56 | 67 | 73 | 77 | |
| Fe2O3 | 0.8 (CaO12%) | 1.0 | 0.8 | 0.7 | 0.7 | 0.5 | |
| Main Applications | Ceramic Roller Kiln Reheating Reheating Furnace Blast Furnace Petrochemical Furnace General Industrial Furnace etc. | ||||||